Semiconducting Tailoring and Electrical Properties of A-site Co Substituted Bi0·5Na0·5TiO3-δ Ferroelectric Ceramics

Yuchen Lan,Changlai Yuan,Xiao Liu,Baohua Zhu,Liufang Meng,Changrong Zhou,Fei Liu,Jiwen Xu,Jiang Wang,Guanghui Rao

DOI: https://doi.org/10.1016/j.matchemphys.2020.124100

IF: 4.778

2021-01-01

Materials Chemistry and Physics

Abstract:The new (1-x) Bi0.5Na0.5TiO3-xCoTiO(3-delta) ferroelectric semiconductor ceramics were prepared successfully by the solid-state method. The single perovskite structures and long-range polarity order of the (1-x) Bi0.5Na0.5TiO3-xCoTiO(3-delta) semiconductor ceramics were observed by X-ray diffraction (XRD) and Raman spectra, respectively. The typical relaxation behavior was founded in all the ceramics. The perfect ferroelectric loops and outstanding optical properties were achieved in the (1-x) Bi0.5Na0.5TiO3-xCoTiO(3-delta) ceramics. A very small optical bandgap (E-g = 1.44 eV) was obtained in the 0.94Bi(0.5)Na(0.5)TiO(3)-0.06CoTiO(3-delta) ceramic, which is approximately 55% lower than that of pure BNT (E-g = 3.2 eV). The J(sc) and V-oc of poled 0.94Bi(0.5)Na(0.5) [Ti-0.71(4+), Ti-0.29(3+)]O-2.71-0.06Co [Ti-0.71(4+), Ti-0.29(3+)]O-2.71 ceramic can reach similar to 1.00 nA/cm(2) and 0.13 V, respectively. The activation energies of the grains and grain boundaries were calculated to be 0.48 and 0.52 eV, respectively. These results show that the Co substation BNT ceramics highlight a promising candidate for multi-functional photoelectric applications.