Abstract:Natural porous mineral supported (TiO2/diatomite) photocatalyst was prepared via a modified sol–gel method using titanium (IV) butoxide (TBOT) and diatomite. The effect of TBOT dosage on adsorption capacity and photocatalytic activity for Rhodamine B (RhB) solution was investigated. The morphology and elemental distribution were determined by scanning electron microscopy with attached energy-dispersive X-ray detector. The porous and crystalline structures were characterized using nitrogen adsorption–desorption and X-ray diffraction techniques, respectively. The prepared TiO2/diatomite hybrid catalyst has shown relatively even porous structure and dispersion of TiO2 over the surface. This suggests that the diatomite matrix prevented the agglomeration of TiO2 particles. Initially, the surface area and pore volume of the hybrid catalyst were increased by adding TBOT then decreased for dosages higher than 1.0ml. The crystalline size of TiO2 immobilized on diatomite matrix by sol–gel method was around 20nm. When the experiments were carried out in the absence of diatomite, this value was increased to 33.73nm. The use of diatomite also promoted an increase of the transformation temperature of the crystalline phase anatase to rutile for the TiO2. The as-prepared TiO2/diatomite composite exhibited high photocatalytic activity (96.0% for 0.5h UV-light irradiation) for the degradation of RhB from wastewater as a result of its unique porous structure and optimum TiO2 loading. In addition, it can be easily separated from suspension and possess a good durability. This hybrid material holds great promise in the engineering field for the environmental remediation.

Substitutionally Rhodium(iv)-Doped Titania Showing Photocatalytic Activity Toward Organics Oxidation under Visible-Light Irradiation

A Visible Light-Driven Titanium Dioxide Photocatalyst Codoped with Lanthanum and Iodine: an Application in the Degradation of Oxalic Acid

Synergistic Photosensitized Removal of Cr(VI) and Rhodamine B Dye on Amorphous TiO2 under Visible Light Irradiation.

Photocatalytic Degradation of Rhodamine B on Co-doped TiO_2 Thin Film under Visible Light

Doping Rh into TiO 2 as a visible-light-responsive photocatalyst: The difference between rutile and anatase

Fabrication of titania thin film with composite nanostructure and its ability to photodegrade rhodamine B in water

Synthesis of Natural Porous Minerals Supported Tio2 Nanoparticles and Their Photocatalytic Performance Towards Rhodamine B Degradation

Photocatalytic Degradation of Organic Dyes by a High Efficient TiO<sub>2</sub>-Based Catalysts Under Solar Light Irradiation

Ti3+ Self-Doping of TiO2 Boosts Its Photocatalytic Performance: A Synergistic Mechanism

Visible Light Cr(VI) Reduction and Organic Chemical Oxidation by TiO2 Photocatalysis.

Synthesis, characterization and application of iodine modified titanium dioxide in phototcatalytical reactions under visible light irradiation

Degradation and Adsorption of Rhodamine B and Phenol on TiO 2 /MCM-41

Preparation and Characterization of Bi3+‐TiO2 and Its Photocatalytic Activity

Synthesis, structural characterization, and application of N-doped TiO2 photocatalyst in degradation of RhB under visible-light irradiation

Rational Design of Zirconium-doped Titania Photocatalysts with Synergistic Brønsted Acidity and Photoactivity.

Light-driven removal of rhodamine B over SrTiO3 modified Bi2WO6 composites

Synthesis and studies of the visible-light photocatalytic properties of near-monodisperse Bi-doped TiO2 nanospheres

Degradation of Rhodamine B by Highly Efficient Photocatalyst TiO<sub>2</sub>-Ag/Ag<sup>+</sup> under Simulated Sunlight Irradiation

TiO 2 /T-PVA Composites Immobilized on Cordierite: Structure and Photocatalytic Activity for Degrading RhB under Visible Light

Controllable Synthesis and Tunable Photocatalytic Properties of Ti3+-doped TiO2

A Direct Synthesis of B-doped TiO2 and Its Photocatalytic Performance on Degradation of RhB