Abstract:P-doped TiO2 nanoparticles were synthesized by the sol-gel method with various H3PO4 amounts. The samples were calcinated at different temperature and charactered by XPS, ICP, XRD, SEM, Raman, FTIR, and UV-vis methods, so that the formation process of phosphate species could be inspected. The XRD results show that P species hinder the particle growth of anatase and increase the anatase-to-rutile phase transformation temperature to more than 900 degrees C, and a new titanyl phosphate, Ti5O4(PO4)(4), was observed in P-doped TiO2 when calcined at 1000 degrees C. The UV-vis results indicate that the P species is likely to have two different states, leading to the variety of visible-light photocatalytic activity and band gap energy of P-doped TiO2. One state is the "separated phase". In this state, the P/Ti ratio is very low so that the P species is surrounded by TiO2. The "separated phase" of P species introduces oxygen into TiO2 lattice and hence causes a red-shift of the adsorption band edge of anatase, leading to the increased visible-light photocatalytic activity of P-doped TiO2. The other state is the "congregated phase". It appears at the micro region where the ratio of P/Ti is high enough to make the TiO2 clusters isolated by P species. The "congregated phase" of P species acts as the interface phase between TiO2 clusters and strongly retards the crystal growth of anatase, resulting in the widened band gap of P-doped TiO2. Furthermore, a possible mechanism was also proposed to explain the formation of the two phases during the sol-gel process. The results indicate that in order to improve the visible-light photocatalytic activity of P-doped TiO2 the percentage of "separated phase" in P species needs to be enhanced.

Doping Rh into TiO 2 as a visible-light-responsive photocatalyst: The difference between rutile and anatase

Facile Fabrication of N-doped TiO2 Nanocatalyst with Superior Performance under Visible Light Irradiation

Photocatalytic degradation of dyestuff wastewater under visible light irradiation using micron-sized mixed crystal TiO2 powders

Simultaneous Structural and Electronic Engineering on Bi- and Rh-co-doped SrTiO3 for Promoting Photocatalytic Water Splitting

Enhanced UV Photoactivity of Ti3+ Self-Doped Anatase TiO2 Single Crystals Hydrothermally Synthesized Using Ti-H2O2-HF Reactants

Photocatalytic Degradation of Rhodamine B on Co-doped TiO_2 Thin Film under Visible Light

A facile synthesis of hierarchical TiO2 for dye adsorption and photocatalysis

Solar photocatalytic degradation of dye wastewater in the presence of heat‐treated anatase TiO<sub>2</sub>powder

A Visible Light-Responsive TiO 2 Photocathode Achieved by a Rh Dopant

Effect of the P/Ti Ratio on the Visible-Light Photocatalytic Activity of P-Doped Tio2

Synergistic Photosensitized Removal of Cr(VI) and Rhodamine B Dye on Amorphous TiO2 under Visible Light Irradiation.

Facile Synthesis of Ni-doped TiO2ultrathin Nanobelt Arrays with Enhanced Photocatalytic Performance

Synthesis of Natural Porous Minerals Supported Tio2 Nanoparticles and Their Photocatalytic Performance Towards Rhodamine B Degradation

Controllable Synthesis and Tunable Photocatalytic Properties of Ti3+-doped TiO2

Efficient Photocatalytic Hydrogen Production over Rh‐Doped Inverse Spinel Zn2TiO4

Facile Synthesis of Anatase–Rutile Diphase N-doped TiO2 Nanoparticles with Excellent Visible Light Photocatalytic Activity

Efficient defect engineering and in-situ carbon doping in ultra-fine TiO2 with enhanced visible-light-response photocatalytic performance

High Photocatalytic Activity Of Rutile Tio2 Induced By Iodine Doping

Manipulating the electronic and photocatalytic properties of anatase TiO2 by metalloid doping

Rh Single Atoms on TiO2 Dynamically Respond to Reaction Conditions by Adapting Their Site

A Crucial Role of Rh Substituent Ion in Photoinduced Internal Electron Transfer and Enhanced Photocatalytic Activity of CdS-Ti(5.2-x)/6 Rhx /2 O2 Nanohybrids