Abstract:Fe/N/C catalysts, synthesized through the pyrolysis of Fe-doped metal-organic framework (MOF) precursors, have attracted extensive attention owing to their promising oxygen reduction reaction (ORR) catalytic activity in fuel cells and/or metal-air batteries. However, post-treatments (acid washing, second pyrolysis, and so on) are unavoidable to improve ORR catalytic activity and stability. The method for introducing Fe3+ sources (anhydrous FeCl3) into the MOF structure, in particular, is a critical step that can avoid time-consuming post-treatments and result in more exposed Fe-Nx active sites. Herein, three different Fe doping strategies were systematically investigated to explore their influence on the types of active sites formed and ORR performance. Fe-NC(Zn2+), synthesized by one-step pyrolysis of Fe doped ZIF-8 (Zn2+) precursor which was obtained by adding the anhydrous FeCl3 source into the Zn(NO3)2•6H2O/methanol solution before mixing, possessed the highest Fe-Nx active sites due to the high-efficiency substitution of Zn2+ ions with Fe3+ ions during ZIF-8 growth, the strong interaction between Fe3+ ions and N atoms of 2-Methylimidazole (2-MIm), and ZIF-8's micropore confinement effect. As a result, Fe-NC(Zn2+) presented high ORR activity in the entire pH range (pH = 1, 7, and 13). At pH = 13, Fe-NC(Zn2+) exhibited a half-wave potential (E1/2) of 0.95 V (vs. reversible hydrogen electrode), which was 70 mV higher than that of commercial Pt/C. More importantly, Fe-NC(Zn2+) showed superior ORR stability in neutral media without performance loss after 5,000 cycles. A record-high open-circuit voltage (1.9 V) was obtained when Fe-NC(Zn2+) was used as a cathodic catalyst in assembled Mg-air batteries in neutral media. The assembled liquid and all-solid Mg-air batteries with high performance indicated that Fe-NC(Zn2+) has enormous potential for use in flexible and wearable Mg-air batteries.

Inflating strategy to fabricate highly dispersed Fe, N co-doped hierarchically porous carbon for ORR and supercapacitor

In-situ Coupling FeN Nanocrystals with Fe/Fe3C Nanoparticles to N-doped Carbon Nanosheets for Efficient Oxygen Electrocatalysis

Rational design of Fe, N co-doped porous carbon derived from conjugated microporous polymer as an electrocatalytic platform for oxygen reduction reaction

An organic-inorganic hybrid strategy to fabricate highly dispersed Fe2C in porous N-Doped carbon for oxygen reduction reaction and rechargeable zinc-air battery

Porous Core-Shell Fe3C Embedded N-doped Carbon Nanofibers as an Effective Electrocatalysts for Oxygen Reduction Reaction

Fabricating hierarchically porous and Fe3C-embeded nitrogen-rich carbon nanofibers as exceptional electocatalysts for oxygen reduction

Highly dispersed γ-Fe2O3 embedded in nitrogen doped carbon for the efficient oxygen reduction reaction

Multiscale porous Fe-N-C networks as highly efficient catalysts for the oxygen reduction reaction

Influence of different Fe doping strategies on modulating active sites and oxygen reduction reaction performance of Fe, N-doped carbonaceous catalysts

Highly Strong Interaction between Fe/Fe3C Nanoparticles and N-Doped Carbon toward Enhanced Oxygen Reduction Reaction Performance

Highly Strong Interaction between Fe/Fe<sub>3</sub>C Nanoparticles and N-Doped Carbon toward Enhanced Oxygen Reduction Reaction Performance

Porous Fe, Co, and N-co-doped Carbon Nanofibers As High-Efficiency Oxygen Reduction Catalysts

MOF-Derived Isolated Fe Atoms Implanted in N-Doped 3D Hierarchical Carbon as Efficient ORR Electrocatalyst in Both Alkaline and Acidic Media.

Co–Fe Alloy Nanoparticles and Fe3C Nanocrystals on N-doped Biomass-Derived Porous Carbon for Superior Electrocatalytic Oxygen Reduction

Fe/Fe3c/N-Doped Carbon Materials from Metal-Organic Framework Composites As Highly Efficient Oxygen Reduction Reaction Electrocatalysts

Fe/N Co-Doped Hierarchically Porous Carbon on N-doped Carbon Nanotubes Towards Oxygen Reduction Reaction

Electron Reservoir Effect of Adjacent Fe Nanoclusters Boosts Atomic Fe Active Sites on Porous Carbon for the Both Electrocatalytic Oxygen Reduction and CO2 Reduction Reaction

Construct N -doped carbon anchored CoFe alloy nanoparticles with high content graphitic-N for electrocatalytic oxygen reduction

Encapsulation of Fe Nanoparticles into an N-doped Carbon Nanotube/nanosheet Integrated Hierarchical Architecture As an Efficient and Ultrastable Electrocatalyst for the Oxygen Reduction Reaction.

A hierarchically ordered porous Fe, N, S tri-doped carbon electrocatalyst with densely accessible Fe-N active sites and uniform sulfur-doping for efficient oxygen reduction reaction

Γ-Fe2o3 Clusters Embedded in 1D Porous N-doped Carbon Matrix As Ph-Universal Electrocatalyst for Enhanced Oxygen Reduction Reaction