Abstract:Heat treatment is the most common method to relieve residual stress and to adjust tensile properties in additively manufactured material. However, the well-known strengthening factors (e.g., dislocation density, cellular sub- structure, low angle grain boundaries, nano-oxide particle) in selective laser melted 316 L (SLM 316 L) are strongly influenced by heat-treatment temperature. In this work, horizontal and vertical oriented SLM 316 L specimens are heat treated from 550 degrees C to 1150 degrees C, followed by tensile tests and microstructural characteriza- tion. With increasing temperature, strength (e.g., yield strength, ultimate tensile strength) is found to decrease and elongation is found to increase. The heat treatments of 550 degrees C, 650 degrees C and 750 degrees C lead to coarsening of cellular sub-structure. Furthermore, the cellular sub-structure and melt boundaries annihilate at 950 degrees C. When the temperature reaches 1150 degrees C, SLM 316 L has finished recrystallization with volume fraction of nano-oxide particles increasing greatly. Based on microstructural characterization, the proposed relationship, considering strengthening mechanisms of cellular sub-structure, nano-oxide particle and grain boundaries, give satisfactory accuracy to predict yield strength for horizontal orientation. The yield strength for vertical orientation can also be predicted by this relationship when modified by consideration of anisotropy of columnar grains and lack-of- fusion defects. The anisotropy and lack-of-fusion lead to 5.4% reduction in yield strength for the vertical orientation. This work establishes quantitative relationships for heat treatment-microstructure-property, in which the anisotropy of tensile properties is considered.

Influence of processing parameters of selective laser melting on high-cycle and very-high-cycle fatigue behaviour of Ti-6Al-4V

The Low-Cycle Fatigue Behavior, Failure Mechanism and Prediction of SLM Ti-6Al-4V Alloy with Different Heat Treatment Methods

Processing Parameter Effects on Residual Stress and Mechanical Properties of Selective Laser Melted Ti6Al4V

Deformation Mechanisms of Selective Laser Melted 316l Austenitic Stainless Steel in High Temperature Low Cycle Fatigue

Experimental Characterization and Strengthening Mechanism of Process-Structure-property of Selective Laser Melted 316 L

Fatigue behavior of selective laser melted 316L stainless steel: experiments and modeling

Fatigue properties of selective laser melted Ti-6Al-4V alloy subjected to laser shock processing

Study of residual stress in selective laser melting of Ti6Al4V

Effects of heat treatment and hot isostatic pressing on microstructure and fatigue improvements in Ti-6Al-4V alloy fabricated by selective laser melting

Role of processing parameters on relative density, microstructure and mechanical properties of selective laser melted titanium alloy

Process parameter optimization for selective laser melting Ti-6Al-4V with high layer thickness

Analysis of Fatigue Properties of Selective Laser Melting 316L Stainless Workpiece After Post-heat Treatment

Fatigue behaviour of selective laser melting steel components

Investigation of fatigue behavior of laser powder bed fusion Ti-6Al-4V: Roles of heat treatment and microstructure

Effect of Processing Parameters on Tensile Properties and Microstructure of Selective Laser Melted AlSi10Mg Alloy

The influence of building direction on the fatigue crack propagation behavior of Ti6Al4V alloy produced by selective laser melting

Study on the effects of the processing parameters on the single tracks and the block support structures fabricated by selective laser melting

Tensile Behavior of Ti-6Al-4V Alloy Fabricated by Selective Laser Melting: Effects of Microstructures and As-Built Surface Quality

High Cycle Fatigue Performance of AlSi10mg Alloy Produced by Selective Laser Melting

Experimental Study of Performance of Ti-6Al-4V Femoral Implants Using Selective Laser Melting (SLM) Methodology

Selective laser melting processing of heterostructured Ti6Al4V/FeCoNiCrMo alloy with superior strength and ductility