Abstract:Exchange bias has increasingly practical significance in magnetoresistive and spintronic devices. However, the underlying mechanism of exchange bias in bulk compounds with the structural single-phase and inhomogeneous magnetic phases is still elusive. Herein, based on experimental and simulation results, two important parameters are studied, i.e., the antiferromagnetic (AFM) volume fraction and the ferromagnetic (FM)/AFM interface area, which essentially determine the (spontaneous) exchange bias of Mn-rich Ni44Co6Mn44-xSn6+x (x = 0 similar to 6) magnetic shape memory alloys. The substitution Sn for Mn changes magnetic ground state following the sequence of superparamagnetic/AFM -> dilute spin glass/AFM -> transition zone -> cluster spin glass/AFM -> FM, accompanying the growth of FM cluster and the weakening of AFM interactions. The results reveal that the magnetic ground state for exchange bias is optimized at transition zone between dilute spin glass/strong AFM and cluster spin glass/weak AFM, in which the optimal AFM volume fraction and FM/AFM interface area are achieved by tuning magnetic fields. A giant exchange bias field of 702.7 mT and a spontaneous exchange bias field of 318.7 mT are demonstrated. The work contributes to in-depth understanding of (spontaneous) exchange bias in magnetically inhomogeneous compounds. Exchange bias has been investigated in Ni44Co6Mn44-xSn6+x alloys. This work reveals that the AFM volume fraction and the FM/AFM interface area essentially determine (spontaneous) exchange bias of Mn-rich Ni44Co6Mn44-xSn6+x (x = 0 similar to 6) magnetic shape memory alloys, which can be optimized by tuning the magnetic ground state (composition x) and magnetic field. image

Tuning The Exchange Bias Effect Via Thermal Treatment Temperature In Bulk Ni50mn42in3sb5 Heusler Alloys

Different Exchange Bias Behavior Caused by Tuning Glassy State in Ni50Mn37Ga13 Ribbons

The Spin Glass and Zero-Field Cooling Exchange Bias Effect Observed above the Curie Temperature in Ni2MnSb Polycrystalline Heusler Alloy

A Room Temperature Exchange Bias Effect Caused by the Coexisting Martensitic Phase Structures in Ni50Mn38Sb12-xGax Polycrystalline Heusler Alloys

Tuning Exchange Bias Through Zero Field Cooling from Different Remanent States above Blocking Temperature in Ni50mn36sb14 Alloy

Spin Cluster Size Dependence of Exchange Bias Effect in Mn50Ni40Ga10 Heusler Alloys

Superposition of Conventional and Spontaneous Exchange Bias in a Ni50Mn34In13Fe3 Magnetic Shape Memory Alloy

Giant Spontaneous Exchange Bias Triggered By Crossover Of Superspin Glass In Sb-Doped Ni50mn38ga12 Heusler Alloys

A Giant Exchange Bias Effect Due to Enhanced Ferromagnetism Using a Mixed Martensitic Phase in Ni50Mn37Ga13 Spun Ribbons

Engineering the Exchange Bias and Bias Temperature by Modulating the Spin Glassy State in Single Phase Bi9Fe5Ti3O27.

Tailoring exchange bias in reentrant spin glass by ferromagnetic cluster size engineering

Large Exchange Bias Triggered by Transition Zone of Spin Glass

Effect of Thermal Cycle on the Interfacial Antiferromagnetic Spin Configuration and Exchange Bias in Ni-Mn-Sb Alloy

Exchange Bias and Its Training Effect in the Martensitic State of Bulk Polycrystalline Ni49.5Mn34.5In16

Large spontaneous exchange bias and giant magnetoresistance in Ni50Mn37−xFexIn13(x=2–4) Heusler alloys

The Martensitic Structures, Exchange Bias Effect and Training Effect in Ni-Mn-Ga Ribbons

Magnetic Phase Separation And Exchange Bias In Off-Stoichiometric Ni-Mn-Ga Alloys

Enhanced room temperature exchange bias caused by antiferromagnetism strengthening

Large exchange bias in magnetic shape memory alloys by tuning magnetic ground state and magnetic-field history

Exchange Bias in Co/CoO Core-Shell Nanowires: Roles of Antifer-Romagnetic Grain Size Distribution and Interfacial Spin Glass

Giant Exchange Bias by Tuning Co/CoO Core/shell Structure