Abstract:Single-phase Li0.5-0.5xZnxFe2.5-0.5xO4 (where x=0.0, 0.2, 0.3, 0.4, 0.5 and 0.8) nanofibers with diameters of 50 similar to 100 nm were successfully fabricated via electrospinning technique in combination with subsequent heat treatment using polyvinylpyrrolidone, nickel nitrate, zinc nitrate and ferric nitrate as principal raw material. The thermal decomposition process of as-spun precursor nanofibers and the influences of the calcination temperature and chemical composition on the crystal structure, micromorphology and magnetic properties of the prepared nanofiber samples were investigated by means of thermogravimetric and differential thermal analysis, X-ray diffraction, field emission scanning electron microscopy, transmission electron microscopy and vibrating sample magnetometer. The results indicate that the pure crystalline LiZn ferrite nanofibers are basically formed when the precursor nanofibers are calcined at 350 degrees C for 2 h. As the calcination temperature increases from 350 to 600 degrees C, the average grain size of Li0.35Zn0.3Fe2.35O4 nanofibers ranges from 13.0 to 47.5 nm and the micromorphology evolves toward a chain-like structrue. The saturation magnetization of the samples monotonously increases from 39.7 to 84.5 A.m(2).kg(-1), while the coercivity increases initially, reaches a maximun value of 12.6 kA.m(-1) at 550 C and then decreases, which reveals that the magnetic single-domain critical size of Li0.35Zn0.3Fe2.35O4 nanofibers may be around 35 nm. The lattice constant of as-prepared Li0.5-0.5xZnxFe2.5-0.5xO4 nanofibers calcined at 500 degrees C for 2 h exhibits an almost linear increase with increasing x and complies with Vegard's law. The coercivity of these nanofiber samples gradually decreases from 17.1 kA.m(-1) for x=0.0 to 2.4 kA.m(-1) for x=0.8, and the saturation magnetization firstly increases to 74.7 A.m(2).kg(-1) with the value of x up to 0.3 and then decreases beyond this limit. Compared to the nanoparticle counterparts prepared under similar conditions, the LiZn ferrite nanofibers have a relatively high coercivity due to their large shape anisotropy. These LiZn ferrite nanofibers have potential application in many fields such as nanoelectronic devices, sensitive devices, microwave absorbers, and biomedicine.

Electrochemical and Magnetic Properties of Electrospun SmFeO3 and SmCoO3 Nanofibers

Ferromagnetic Fe3O4 Nanofibers: Electrospinning Synthesis and Characterization

Electrochemical and Magnetic Properties of Perovskite-Type PrFeO3 and EuFeO3 Nanofibers

Syntheses, Characterization, Magnetic, and Electrochemical Properties of Perovskite‐type NdFeO3 and NdCoO3 Nanofibers

Preparation And Properties Of Sm, Nd Co-Doped Ceo2 Nanofiber Electrolyte

Electrospinning Fabrication, Characterization and Magnetic Properties of Co0.5Ni0.5Fe2O4 Nanofibers

Electrospun Magnetic SrFe12O19nanofibres with Improved Hard Magnetism

Preparation and Magnetic Properties of Electrospun FeCo Nanofibres

Perovskite-type RCoO3 (R = Pr, Eu, Gd) nanofibers for supercapacitor electrodes and antiferromagnet

Perovskite-type RCoO 3 (R = Pr, Eu, Gd) Nanofibers for Supercapacitor Electrodes and Antiferromagnet

Structure and Magnetic Properties of Electrospun Co0.6Ni0.3Zn0.1Fe2O4 and Co0.6Ni0.3Cu0.1Fe2O4 Nanofibers

Improvement in Structural and Magnetic Properties of Electrospun Ni&lt;sub&gt;1-x&lt;/sub&gt;Cu&lt;sub&gt;x&lt;/sub&gt;Fe&lt;sub&gt;2&lt;/sub&gt;O&lt;sub&gt;4&lt;/sub&gt; Nanofibers

Electrospinning Of Fe, Co, And Ni Nanofibers: Synthesis, Assembly, And Magnetic Properties

Study on the structure and magnetic properties of Ni0.3Zn0.6Cu0.1Sm0.05Fe1.95O4 nanofibers

Electrospinning Preparation, Structural and Magnetic Properties of Li0.5-0.5xznxfe2.5-0.5xo4 Nanofibers

Electrochemical and DFT investigations of light rare earth chromite nanofibers

Magnetic and microwave absorption properties of electrospun Co 0.5Ni0.5Fe2O4 nanofibers

Electrochemical and magnetic properties of perovskite type RMnO<sub>3</sub> (R = La, Nd, Sm, Eu) nanofibers

Photocatalytic and Magnetic Behaviors Observed in BiFeO3 Nanofibers by Electrospinning

Electrospinning preparation, characterization and magnetic properties of cobalt-nickel ferrite (Co 1-xNi xFe 2O 4) nanofibers

Robust SiO2-modified CoFe2O4 hollow nanofibers with flexible room temperature magnetic performance.