Atomic Layer Deposition onto Thermoplastic Polymeric Nanofibrous Aerogel Templates for Tailored Surface Properties
Jianwei Lu,Yi Li,Wei Song,Mark D. Losego,Rebhadevi Monikandan,Karl I. Jacob,Ru Xiao
DOI: https://doi.org/10.1021/acsnano.9b09497
IF: 17.1
2020-07-09
ACS Nano
Abstract:Poly(vinyl alcohol-<i>co</i>-ethylene) (EVOH) nanofibrous aerogel (NFA) templates were fabricated through vacuum freeze-drying from EVOH nanofibrous suspensions. Aluminum oxide (Al<sub>2</sub>O<sub>3</sub>) layers were deposited onto highly porous templates to form organic–inorganic hybrid aerogels by the atomic layer deposition (ALD) technique. Chemical and physical measurements showed that mechanical properties were improved through ALD. In addition, the surface chemistry of ALD modified aerogels showed a fascinating cyclic change based on the number of ALD deposition cycles. A transition from hydrophilicity to hydrophobicity was observed after a few cycles of ALD coating; however, additional deposition cycles changed the wettability characteristics back to hydrophilicity. This hydrophilic–hydrophobic–hydrophilic variation is shown to be governed by a combination of geometrical and chemical surface properties. Furthermore, the deposited Al<sub>2</sub>O<sub>3</sub> could substantially improve aerogels strength and reduce permanent deformation after cyclic compression. The Young's modulus of aerogels increased from 5.54 to 33.27 kPa, and the maximum stress at 80% strain went up from 31.13 to 176.11 kPa, after 100 cycles of trimethyl-aluminum (TMA)/water ALD. Thermogravimetric analysis (TGA) results confirm that ALD can effectively improve the heat resistance characteristics of polymeric aerogel. The onset temperature and the residual mass increased with increasing numbers of ALD cycles. During pyrolysis, the nanofiber cores were decomposed, and the brittle pure Al<sub>2</sub>O<sub>3</sub> self-supporting nanotube aerogels with the continuous hollow nanotubular network were formed. A coating of continuous thickness Al<sub>2</sub>O<sub>3</sub> layer on individual nanofiber was achieved after 100 ALD cycles. In additional to mechanical strength and physical property changes, the ALD modified aerogel also shows a superhydrophobic and oleophilic surface chemistry, which could potentially be used to remove oils/organic solvents from water. The resultant aerogels exhibit excellent absorption capacity (31–73 g/g) for various liquids, and the material could be reused after distillation or squeezing. A successful scale-up of such materials could provide some insights into the design and development of thermoplastic polymeric NFAs with substantial industrial applications.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsnano.9b09497?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsnano.9b09497</a>.Figures S1–S18 and Tables S1–S5 showing reaction mechanisms, SEM images, AFM images, XPS spectrum, mechanisms of cross-linking and esterification, dynamic water contact angles, wicking properties, photographs of water absorption, cyclic stress–strain curves, TEM images, onset temperature of weight loss stages, thickness of Al<sub>2</sub>O<sub>3</sub> coatings, physical properties, surface average roughness variations, peak BE and atomic ratio of various aerogels, comparison of sorption capacities (<a class="ext-link" href="/doi/suppl/10.1021/acsnano.9b09497/suppl_file/nn9b09497_si_001.pdf">PDF</a>)Movie S1: Dynamic compressive behavior of 6cy-ALD aerogels under a 60% compressive strain (<a class="ext-link" href="/doi/suppl/10.1021/acsnano.9b09497/suppl_file/nn9b09497_si_002.avi">AVI</a>)Movie S2: Canola oil absorbed by 6cy-ALD aerogels (<a class="ext-link" href="/doi/suppl/10.1021/acsnano.9b09497/suppl_file/nn9b09497_si_003.avi">AVI</a>)Movie S3: Chloroform absorbed by 6cy-ALD aerogels (<a class="ext-link" href="/doi/suppl/10.1021/acsnano.9b09497/suppl_file/nn9b09497_si_004.avi">AVI</a>)This article has not yet been cited by other publications.
materials science, multidisciplinary,chemistry, physical,nanoscience & nanotechnology