Synthesis of Star-Shaped Nanocrystalline Cellulose/Fluorinated Polyacrylate via RAFT-Mediated Emulsion Polymerization and Its Application on Fabric Finishing

Jianhua Zhou,Yan Li,Hongtao Yao,Hong Li,Xiang Li
DOI: https://doi.org/10.1007/s12221-023-00088-w
IF: 2.5
2023-02-24
Fibers and Polymers
Abstract:Nanocrystalline cellulose (NCC), as a kind of robust renewable green nanomaterials, can be used as an emulsion stabilizer and a reinforcing filler for coatings. However, the high polarity of NCC limits its interfacial interaction and dispersion with non-polar polymers. This work presented an environmentally friendly and simple strategy to generate star-shaped nanocrystalline cellulose/fluorinated polyacrylate with outstanding water–oil repellent properties and mechanical property via RAFT-mediated emulsion polymerization using poly(acrylic acid)- b -poly(hexafluorobutyl acrylate)- g -nanocrystalline cellulose particles as stabilizers. The influences of the HFBA content and pH value on emulsion polymerization and nanocomposite film properties were systematically studied. The influences of the HFBA content and pH value on the emulsion polymerization process and the surface properties of the latex films were discussed. The results showed that the nanocrystalline cellulose/fluorinated polyacrylate emulsion with good stability was prepared under the condition that when the pH value was 9.26, HFBA content was 10 wt%, and the water contact angle and oil contact angle of the nanocomposite film were 110.8° and 95°, respectively. The chemical structure of star-shaped nanocrystalline cellulose/fluorinated polyacrylate was confirmed by 1 H-NMR and FT-IR spectroscopy, respectively. The thermal stability of the latex film was raised remarkably with the increase of HFBA content. AFM measurement results indicated that nanocrystalline cellulose particles could improve the roughness of the nanocomposite film. And the roughness of the nanocomposite film increased with the increase of the content of PAA- b -PHFBA- g -NCC particles. The results showed that the finished fabric had excellent softness, washing resistance, water and oil resistance.
materials science, textiles,polymer science
What problem does this paper attempt to address?