Residual Fracture Energy of Concrete Suffering from Fatigue Loading

Mengdi Jia,Zhimin Wu,Rena C. Yu,Xiaoxin Zhang

DOI: https://doi.org/10.1016/j.engfracmech.2021.107956

IF: 5.4

2021-01-01

Engineering Fracture Mechanics

Abstract:To investigate the degradation of the residual fracture energy of concrete suffering from fatigue loading, 150 three-point bending (TPB) beams were first subjected to a fatigue load until the preset number of fatigue cycles was reached, and then the static load was applied to these specimens until failure occurred. Based on the equilibrium relationship between the energy dissipated by the fatigue fracture process zone (FPZ) under static loading and the external work, a calculation method for the residual fracture energy of concrete suffering from fatigue loading was proposed. The effects of the number of fatigue cycles, the fatigue crack opening displacement, and the fatigue load level on the residual fracture energy of concrete were evaluated, and an empirical model for predicting the residual fracture energy was proposed. The results showed that in the initial stage of fatigue loading, there was a rapid drop of the residual fracture energy with a decelerated degradation rate. With the increases of the number of fatigue cycles and the fatigue crack opening displacement, a stable degradation stage of the residual fracture energy with an approximately constant degradation rate was observed. Furthermore, with the decreasing fatigue load level, the residual fracture energy increased for the same fatigue cycles, while the residual fracture energy decreased for the same fatigue crack opening displacement. The residual fracture energy obtained in this study is essential for the numerical calculation of the residual bearing capacity of concrete structures.