Abstract:The GH4169 nickel-based superalloy is a type of alloy that exhibits excellent properties. It has high creep strength, fracture strength, as well as good corrosion resistance, fatigue resistance, and oxidation resistance under high-temperature conditions, allowing it to be widely used in the aerospace, nuclear reactor, and oil industries. However, it is challenging to process superalloys because of their high hardness and considerable processing wastes, such as cutting fluid. Many processing wastes cannot be directly used for remelting due to issues like surface stains. However, the production of GH4169 superalloys requires low carbon content for recycling, so the alloy scraps that meet the standard after pre-cleaning can be obtained. This study explores the ultrasonic cleaning effect of superalloy scraps with different liquid-solid ratios, cleaning times, and cleaning temperatures to obtain the optimal cleaning conditions of GH4169 superalloy scraps. The content of carbon in unwashed superalloy scraps is as high as 0.2%, far exceeding the carbon content of the alloy itself (0.015–0.036%). After ultrasonic cleaning at 60 °C for 30 min with a cleaning solution having a solid-liquid ratio of 1:2.5, the carbon content of the scraps decreased from over 0.2%–0.048%, and the decarburization rate reached above 77%. After remelting the cleaned scraps into alloy bars, the composition content and properties of the bars meet the production requirements. The cleaning mechanism is analyzed, and the cavitation effect, saponification, and emulsification mode in the ultrasonic cleaning process are explained. This paper positively promotes recycling GH4169 nickel-based superalloy waste to protect environmental resources.

Selective Extraction of Ni from Superalloy Scraps by Molten Mg-Zn

Dealloying Superalloy by Liquid Mg for the Selective Extraction of Ni

Clean Recycling of Spent Nickel-Based Single-Crystal Superalloy by Molten Magnesium

Recovery of valuable metals from electroplating sludge with reducing additives via vitrification

Separation of nickel, cobalt and magnesium from the spent MH-NI and CD -NI battery anode materials

Comprehensive Recovery of Copper-Nickel Alloy Scrap

Extraction of Non-metallic Inclusions in Nickel-Based Superalloy Powders by Stepwise Acid Dissolution Method

Separation and Recovery of Iron and Nickel from Low-Grade Laterite Nickel Ore by Microwave Carbothermic Reduction Roasting

Separation of Magnesium Impurity from Nickel and Cobalt Mixtures Using Ethylenediaminetetraacetic Acid and Temperature Optimization

Extraction, phase transformation and kinetics of valuable metals from nickel-chromium mixed metal oxidized ore

Compound purification of nickel base superalloy cutting waste through special cleaning agent attached to ultrasonic stirring

Magnetic separation of nickel-plating waste liquid using a high temperature superconducting bulk magnet

Liquid-solid phase separation and recycling of permalloys in liquid Mg

Recovery of Cu and Ni in Electroplating Sludge by a Low-Temperature Alkaline Smelting Technique

Stepwise separation and recovery of molybdenum, vanadium, and nickel from spent hydrogenation catalyst

Novel and efficient purification of scrap Al-Mg alloys using supergravity technology

On the Production of Mg-Nd Master Alloy from Ndfeb Magnet Scraps

Electrochemical Dissolution of MCrAlY Coatings and Oxide Layers on Ni-based Superalloys in 3.5% NaCl and Aqua-Regia Solutions

New Slag for Nickel Matte Smelting Process and Subsequent Fe Extraction

Simultaneous extraction and separation of Ni(OH) 2 , Ni powder and Ni plate from waste nickel-cobalt scrap in one spot: Control sequence of electrical reduction

Extraction of Cu and Ni from Low-Ni Matte by a Combined Chemical Precipitation and Molten Salt Electrolysis Approach