Flame spray pyrolysis synthesis and H₂S sensing properties of CuO-doped SnO₂ nanoparticles

Zhicheng Chen,Zuwei Xu,Haibo Zhao

DOI: https://doi.org/10.1016/j.proci.2020.06.315

IF: 6.535

2021-01-01

Proceedings of the Combustion Institute

Abstract:In this work, CuO-doped SnO2 (CuO/SnO2) nanoparticles with different CuO mass fractions (0-1.0 wt%) are synthesized by a flame spray pyrolysis (FSP) route and applied to fabricate thin-film gas sensors for H2S detecting. The nanoparticles are characterized by X-ray diffraction (XRD), N-2-physisorption isotherms, transmission electron microscopy (TEM) and X-ray photoelectron spectroscopy (XPS). Within the 0-1.0 wt% CuO-doping concentrations, all of the nanoparticles predominantly exhibit a spherical structure with a diameter of 5-15 nm, and possess a quite large specific surface area (110-125 m(2) /g). These textural characterizations suggest that Cu atoms form substitution doping in polycrystalline SnO2 nanoparticles at low CuO levels (< 0.5 wt%), and they are segregated as CuO nanoclusters at high CuO concentrations (0.5-1.0 wt%). From gas-sensing measurements, the CuO doping significantly improves the H2S sensing performance of SnO2 nanoparticles, especially at the optimal CuO-doping mass fraction of 0.5 wt%. The optimal CuO-doped SnO2 gas sensor exhibits a highest response (Ra /Rg = 1056) under a condition of 10 ppm H2S atmosphere at 125 degrees C. This is probably because a large number of highly dispersed small CuO nanoclusters are supported on the surface of the nanoparticle for 0.5 wt% doping, forming abundant p-n junctions with SnO2. When the CuO/SnO2 composite is exposed to H2S, semiconducting CuO is converted to metallic-like CuS, thereby increasing electrical conductivity and resulting in a high response. In addition, the optimal sensor displays good cycle performance and high H2S selectivity against other toxic and flammable gases including NH3, H-2 and CO. Therefore, the gas sensor of 0.5 wt% CuO-doped SnO2 made by the FSP shows a large potential for H2S detecting in practical industrial application. (C) 2020 The Combustion Institute. Published by Elsevier Inc. All rights reserved.