A Polymorphic FeS 2 Cathode Enabled by Copper Current Collector Induced Displacement Redox Mechanism
Lulu Tan,Jinming Yue,Zhao Yang,Xiaogang Niu,Yusi Yang,Jianwen Zhang,Ruiting Wang,Liang Zeng,Lin Guo,Yujie Zhu
DOI: https://doi.org/10.1021/acsnano.1c02438
IF: 17.1
2021-06-28
ACS Nano
Abstract:In this contribution, we fabricated a composite consisting of two polymorphs of FeS<sub>2</sub>, pyrite (P-FeS<sub>2</sub>) and marcasite (M-FeS<sub>2</sub>), for high-performance Li-FeS<sub>2</sub> battery. A series of electrochemical, microscopic, and spectroscopic characterizations indicate that the introduction of metastable M-FeS<sub>2</sub> into P-FeS<sub>2</sub> enables the four-electron reduction between FeS<sub>2</sub> and lithium to generate Fe and Li<sub>2</sub>S, providing a high specific capacity of 894 mAh/g with specific energy over 1300 Wh/kg. Moreover, it is verified that the electrochemical irreversibility of this composite toward lithium storage is mainly rooted in the shuttle effect, caused by the elemental sulfur which is inevitably produced during the oxidation process of Li<sub>2</sub>S and Fe. To tackle this issue, copper (Cu) current collector is adopted to chemically immobilize the soluble lithium polysulfides and fundamentally alter the reaction pathway. It is shown that compared with Fe, Li<sub>2</sub>S prefers to react with Cu current collector to generate Cu<sub>2</sub>S through the thermodynamically facile displacement reaction mechanism benefiting from the similar lattice framework between Cu<sub>2</sub>S and Li<sub>2</sub>S. Such displacement reaction without lattice reconstruction renders the composite superior rate capability (∼730 mAh/ A/g) and long lifespan (89.7% capacity retention after 3200 cycles). Present work allows for the fabrication of high-performance electrodes based on metal chalcogenides.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsnano.1c02438?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsnano.1c02438</a>.Comparison of properties between S and FeS<sub>2</sub>, crystal structure characterization, cycling performance, CV curves, and Nyquist plots of M-FeS<sub>2</sub> and P-FeS<sub>2</sub>. N<sub>2</sub> adsorption–desorption isotherm curves, discharge energy density, discharge–charge profiles, and self-discharge experiments of P/M-FeS<sub>2</sub>. XRD patterns of P/M-FeS<sub>2</sub> and the samples annealed at 450 °C. The galvanostatic charge–discharge curves and cycling performance of Cu<sub>2</sub>S. SEM images and EDS elemental mapping of S on the back of the copper current collector. UV–vis absorbance spectra of the electrolyte (<a class="ext-link" href="/doi/suppl/10.1021/acsnano.1c02438/suppl_file/nn1c02438_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
materials science, multidisciplinary,chemistry, physical,nanoscience & nanotechnology