Abstract:The microstructure, stress rupture properties and deformation mechanisms of a new alloy during long-term aging were investigated. The microstructure evolution mainly included the coarsening of gamma' phase and the precipitation of eta phase. During aging at 700 degrees C, 750 degrees C and 800 degrees C, the coarsening rate k of gamma' phase was about 7.818 nm(3)/h, 42.927 nm(3)/h and 178.226 nm(3)/h, respectively. The activation energy Q for gamma' coarsening was about 279.98 kJ/mol, which meant that element diffusion controlled the coarsening of gamma' phase. After aging at 750 degrees C for 3000 h and 800 degrees C for 2000 h, a new needle-like eta phase was precipitated near GBs and around MC carbides, then grew into the grain interiors. The quantity of eta phase increased with the increase of aging time. With the growth of eta phase, gamma' depleted zones were found around eta phase. This was principally because both gamma' phase and eta phase were enriched in Ni and Ti, and the growing up of I phase absorbed gamma' phase. After aging at 700 degrees C for 300-3000 h and 750 degrees C for 300-2000 h, the stress rupture life at 750 degrees C/430 MPa remained at a high level and most of them were higher than 100 h. That was because the slightly grown-up gamma' phase acted as strong obstacles to the dislocation motion, Orowan bypassing combing stacking fault shearing acted as the dominant mechanism during stress rupture deformation. After aging at 750 degrees C and 800 degrees C for 3000 h, the stress rupture life decreased to 45.7 h and 7.68 h, respectively. One reason was that the seriously grown-up gamma' phase was very hard to impede the dislocation motion, almost all gamma' phases were cut by dislocations with leaving stacking faults inside them during stress rupture deformation. The other reason was that needle-like eta phase promoted dislocation pile-up and contributed to the nucleation of micro-cracks, meanwhile the gamma' depleted zones could be conductive to the propagation of micro-cracks.

Influence of Long-Term Aging on Microstructural Stability and Performance of DD6 Superalloy

Effects of Long-Term Aging on the Microstructures and Tensile Properties of Ni-Based Single Crystal Superalloy

Microstructure Analysis and Life Prediction of DD6 Superalloy under 760 °C Combined High and Low Cycle Fatigue Conditions

Long-term Oxidation Behavior and Mechanism of DD6 Ni-based Single Crystal Superalloy at 1050 °C and 1100 °C in Air

Intermediate Temperature Brittleness and Directional Coarsening Behavior of Nickel-Based Single-Crystal Superalloy DD6

Microscopic Damage and Fracture Mechanism of Nickel-based Single Crystal Superalloy during Low Cycle Fatigue at Elevated Temperature

The Effect of Post-heat Treatment on the Microstructures of Single Crystal DD6 Superalloy

Effect of Aging Heat Treatment on Microstructure of Ni-based Single Crystal Superalloys

Correlations Between Microstructure Evolution and Mechanical Behavior of a Nickel-Based Single Crystal Superalloy with Long-Term Aging Effects

Effect of Aging Time at High Temperature on Microstructural Evolution Behavior of a Nickel-Based Single Crystal Superalloy

Thermal Stability of GH4065A Superalloy Based on Microstructural and Performance Evolution Following Long-Term Aging

Effects of Microstructure Evolution on the Deformation Mechanisms and Tensile Properties of a New Ni-base Superalloy During Aging at 800 °C

Microstructure Evolution of Single Crystal Superalloy DD6 at High Temperature

The Effect of Long-Term Aging on the Microstructure and Properties of a Novel Nickel-Based Powder Superalloy FGH4113A

Effect of Long-Term Aging on the Microstructure, Stress Rupture Properties and Deformation Mechanisms of a New Cast Nickel Base Superalloy

Long-term Aging Behavior and Mechanism of CMSX-4 Nickel-Based Single Crystal Superalloy at 950 ℃ and 1050 ℃

Effect of Long-Term Aging on the Evolution of Γ' and TCP Phases of a Ni3Al Based Single Crystal Superalloy

Long Time Stability of Direct Aging GH4169G Alloy Forging Disc after Thermal Exposure at 650°C

Effect of high temperature aging on microstructures and tensile properties of a selective laser melted GTD222 superalloy

Microstructural Evolution and Hardness of a Heat Resistant Alloy During Long Term Aging at 700 °C

Effects of Heat Treatment Regime on the Size and Amount of Γ′ Phase of DD6 Single Crystal Superalloy