Abstract:Ti6Al4V (Ti64) alloys manufactured by selective laser melting (SLM) are well known for their susceptibility to failure at a low ductility of less than 10% due to the formation of an (α′) martensitic structure. Annealing and solution treatments as post-heat treatments of α′ are considered a good way to improve the mechanical performance of SLM-manufactured Ti64 parts. In this research, the effect of heat treatment parameters such as temperature (850 °C and 1020 °C) and cooling rate (furnace and water cooling) on the microstructure and mechanical properties of the SLM Ti64 structure was investigated. It was shown that the tensile strength/ductility of the Ti64 alloy produced by SLM was determined by the post-heat treatment. The experimental results revealed that heat treatment at 850 °C followed by furnace cooling resulted in the best possible combination of ductility (13%) and tensile strength (σy = 932, σu = 986 MPa) with a microstructure consisting mainly of 78.71% α and 21.29% β. Heat treatment at 850 °C followed by water cooling was characterized by a reduction in hardness and the formation of predominantly α plus α′′ and a small amount of β. HT850WC exhibited yield and tensile strengths of about 870 and 930 MPa, respectively, and an elongation at fracture of 10.4%. Heat treatment at 1020 °C and subsequent cooling in the furnace was characterized by the formation of an α + β lamellar microstructure. In contrast, heat treatment at 1020 °C and subsequent water cooling formed semi-equiaxial β grains of about 170 μm in diameter with longer elongated α grains and basket-weave α′. Post-treatment at 1020 °C followed by furnace cooling showed high ductility with an elongation of 14.5% but low tensile strength (σy = 748, σu = 833 MPa). In contrast, post-treatment at 1020 °C followed by water cooling showed poor ductility with elongation of 8.6% but high tensile strength (σy = 878, σu = 990 MPa). The effect of aging at 550 °C for 3 h and cooling in a furnace on the microstructure and mechanical properties of the specimens cooled with water was also studied. It was found that aging influenced the microstructure of the Ti6Al4V parts, including β, α, and α′′ precipitation and fragmentation or globularization of elongated α grains. The aging process at 550 °C leads to an increase in tensile strength and a decrease in ductility.

Correlation of microstructure and mechanical properties of Ti<sub>2</sub>AlNb manufactured by SLM and heat treatment

Effect of Heat Treatments on the Microstructure and Mechanical Properties of Ti2AlNb Intermetallic Fabricated by Selective Laser Melting

Effect of Heat Treatment on Microstructure and Properties of Ti2AlNb Alloy Formed by Selective Laser Melting

In-situ Study of Microstructure and Mechanical Properties of GH3536 Alloy Manufactured by Selective Laser Melting at 750 °C

Microstructure Evolution and Mechanical Properties of High Nb-TiAl Intermetallic Compounds during Heat Treatment

Microstructure, heat treatment and mechanical properties of TiB2/Al–7Si–Cu–Mg alloy fabricated by selective laser melting

Heat-treatment induced microstructural evolution and enhanced mechanical property of selective laser melted near β Ti-5Al-5Mo-5 V-3Cr-1Zr alloy

Effects of Annealing and Solution Treatments on the Microstructure and Mechanical Properties of Ti6Al4V Manufactured by Selective Laser Melting

Influence of Heat Treatment on Microstructure and Tensile Properties of Selective Laser Melting Metastable Ti55531-0.5Nb Alloy

Effect of Subtransus Heat Treatment on the Microstructure and Mechanical Properties of Additively Manufactured Ti-6Al-4V Alloy

Influence of Post Heat Treatment on Microstructure and Mechanical Property of Ti6Al4V Parts Produced by Selective Laser Melting

Effect of Heat Treatment on Microstructure Evolution and Mechanical Properties of Selective Laser Melted Ti–6Al–4V and TiB/Ti–6Al–4V Composite: A Comparative Study

Microstructural evolution and mechanical properties of Ti55531–0.5Nb fabricated by selective laser melting under different heat treatments

Effects of Post-Heat Treatments on the Microstructure and Mechanical Properties of Ti-6Al-4V Alloy Fabricated by Selective Laser Melting

Microstructural Evolution and Mechanical Behavior of TA15 Titanium Alloy Fabricated by Selective Laser Melting: Influence of Solution Treatment and Aging

Effect of Heat Treatment Patterns on Porosity, Microstructure, and Mechanical Properties of Selective Laser Melted TiB2/Al–Si–Mg Composite

Influence of Heat Treatments on Microstructure and Mechanical Properties of Laser Additive Manufacturing Ti-5Al-2Sn-2Zr-4Mo-4Cr Titanium Alloy

Influence of Heat Treatment on the Microstructure and Mechanical Properties of TC4 Alloy Fabricated by Selective Laser Melting

Effect of Post-Heat Treatment on Ti2AlNb-based Alloy Fabricated by Twin-Wire Alternating Dual-Electron Beam Additive Manufacturing Technology

Investigation on Microstructure and Mechanical Properties of Heat-Treated Ti-47.5Al–3Nb-3.5Cr Alloy

Effects of different heat treatment temperatures on the microstructure and mechanical properties of additive manufacturing Ti65 alloys