Abstract:It is essential to study the tensile fracture mechanism of additively manufactured materials and develop the effective process treatment techniques to improve their fracture resistance. In this paper, the effects of different treatment processes on the microstructure and tensile fracture properties of TC17 titanium alloy melted by laser selective zone melting were investigated. The static tensile fracture morphological characteristics were observed by combining SEM and EDS. The metallographic microstructure after chemical corrosion was observed optically. And the tensile fracture morphology of the three states of TC17 titanium alloy samples at room temperature conditions was investigated. The results show that the metallographic matrix microstructure of TC17 titanium alloy after HT, HIP and HIP-HT treatments was a bimodal structure with α+β phases, i.e., β phase was in the form of a net basket, and α phase was in the form of a coarse bar. The grain sizes of the samples treated by different processes were different, but the difference in grain size of the HT-treated tissues was small, and the difference in grain size of the HIP-HT-treated tissues was large. And the coarse α-phase segregation could be seen at the edge of the samples. The 3D-printed materials had complex changes in anisotropic properties affected by the printing structure and tissue. The printed tissues were brittle and had high internal stresses. These problems were partly improved at high temperatures, but they still existed. The HIP-HT-treated materials had a large α+β-phase bimodal structure. The HT-treated material had coarse grains and precipitation phases, poor room temperature plasticity, and improved high temperature plasticity. After HT treatment, the original printing microstructure changed, the strength and plasticity were significantly improved, but the macroscopic printing structure still had a slight influence on the fracture morphology. When HIP treatment temperature was higher, the influence of macroscopic printing structure basically disappeared, but the grain and microstructure grew up, and the strength and plasticity were slightly lower than that of the HT treatment. HIP process basically eliminated the unfused defects of the three-dimensional morphology, and the local weak bonding zone formed.

Influence of Heat Treatments on Microstructure and Mechanical Properties of Laser Additive Manufacturing Ti-5Al-2Sn-2Zr-4Mo-4Cr Titanium Alloy

Effect of Heat Treatment on Microstructure and Mechanical Properties of Titanium Alloy Fabricated by Laser–Arc Hybrid Additive Manufacturing

Effect of Heat Treatment on the Microstructure and Mechanical Properties of Additive Manufactured Ti-6.5Al-2Zr-1Mo-1V Alloy

Effects of different heat treatment temperatures on the microstructure and mechanical properties of additive manufacturing Ti65 alloys

Effect of heat treatment on microstructure and mechanical properties of laser-deposited Ti65 near-alpha titanium alloy

The Heat Treatment Influence on the Microstructure and Hardness of TC4 Titanium Alloy Manufactured via Selective Laser Melting

Heat-treatment induced microstructural evolution and enhanced mechanical property of selective laser melted near β Ti-5Al-5Mo-5 V-3Cr-1Zr alloy

[Letter: Erythema chronicum migrans meningitis--a bacterial infectious disease? Conclusion to the preceding comments by P. Giroud].

Effects of Heat Treatment on the Microstructure Evolution and Mechanical Properties of Selective Laser Melted TC4 Titanium Alloy

Effect of annealing treatment on microstructure and tensile properties of Ti-48Al-2Cr-5Nb alloy fabricated by laser additive manufacturing

Effects of different treatment processes on microstructure and tensile fracture behaviour of selected laser melting TC17 titanium alloy

Influence of Heat Treatment on the Microstructure and Mechanical Properties of TC4 Alloy Fabricated by Selective Laser Melting

Effect of Solution Aging Heat Treatment on Microstructure Evolution and Properties of TC17 Titanium Alloy Formed by Laser Solid Forming

Effect of Solution and Aging Treatments Parameters on Microstructure and Mechanical Properties of Laser Additive Manufactured Ti-10V-2Fe-3Al Metastable β

Influence of Heat Treatments on Microstructure and Mechanical Properties of Ti⁻26Nb Alloy Elaborated In Situ by Laser Additive Manufacturing with Ti and Nb Mixed Powder

Influence of Heat Treatment on Microstructure and Mechanical Properties of TC4 Fabricated by Laser Melting Deposition

Tailoring the microstructure and mechanical property of laser powder bed fusion fabricated Ti–6Al–2Sn–4Zr–2Mo via heat treatment

Effect of Subtransus Heat Treatment on the Microstructure and Mechanical Properties of Additively Manufactured Ti-6Al-4V Alloy

The effect of heat treatment on corrosion behavior of selective laser melted Ti-5Al-5Mo-5V-3Cr-1Zr alloy

Effect of Heat Treatment on the Microstructure and Hardness of the SLMed TC4 Alloy Specimens

The impact of heat treatment on microstructure, residual stress, and mechanical behavior of laser powder bed fusion additively manufactured Ti–6Al–2Sn–4Zr–2Mo alloy