Abstract:Inconel 718/316L dissimilar welding is widely used in nuclear power plants, which suffers from the deterioration of mechanical properties and corrosion resistance after welding, attributed to the formation of brittle phase and the existence of residual stress. In this paper, the impact of post-weld heat treatment (PWHT) on Inconel 718/316L welding joints is systematically investigated. By conducting PWHT after welding, notable reductions in residual stress in as-welded joints are significantly reduced and the microstructure is improved, resulting in an enhanced strength-ductility synergy and corrosion resistance. The as-welded joints exhibit the generation of brittle Laves phase and welding residual stress in the fusion zone. After PWHT at 650 °C, a substantial increase in the quantity of fine-scale γ″ strengthening phases with a uniform dispersion distribution in weldment is observed, along with the release of residual stress. This combination yields an optimal strength-ductility synergy and corrosion resistance of the joint. However, the δ phase precipitates along in Laves phase boundary after PWHT at 850 °C, which exhibits a semi-coherent interface with γ matrix, and a non-coherent interface with the Laves phase, leading to severe stress concentration at the δ phase interface. This severe stress concentration could be a preferred location for crack initiation and propagation, resulting in a substantial loss in mechanical behavior. Additionally, the increase in the phase boundary of γ/γ″, γ/Laves, Laves/δ and γ/δ reduces the corrosion resistance of the joint. The findings of this study provide an effective strategy for improving the performance of Inconel 718/316L dissimilar laser beam welding joint.

Effect of Multiple Repair Welding on Crack Susceptibility and Mechanical Properties of Inconel 718 Alloy Casting

Effect of Repeated Weld Repairs on Microstructure and Mechanical Properties of Heat-Affected Zone in CA6NM Stainless Steel

Influence of Multiple Repair Welding on Microstructure and Properties of 06Cr19Ni10 Stainless Steel

Hydrogen-assisted fatigue crack propagation bebavior of selective laser–melted Inconel 718 alloy

Improving the strength-ductility synergy and corrosion resistance of Inconel 718/316L dissimilar laser beam welding joint via post-weld heat treatment

The Effect of Precipitates on the Stress Rupture Properties of Laser Powder Bed Fusion Inconel 718 Alloy

Study on the Hot Cracking Law of Inconel 690/52M Welding Material on F304LN Base Metal by Multi-Layer Cladding

An Experimental Investigation of In-Plane Constraint Effect on Local Fracture Resistance of A Dissimilar Metal Welded Joint

Finite element simulation of multi-layer repair welding and experimental investigation of the residual stress fields in steel welded components

Heat-affected Zone Crack Healing in IN939 Repaired Joints Using Hot Isostatic Pressing

Experimental to study the effect of multiple weld-repairs on microstructure, hardness and residual stress for a stainless steel clad plate

A promising strategy of multicomponent alloy intermedium for enhancing the mechanical performance of inertia friction welding joints of Inconel 718 alloys

Microstructure and High-Temperature Mechanical Properties of Inconel 718 Superalloy Weldment Affected by Fast-Frequency Pulsed TIG Welding

Alternatives to Reduce Hot Cracking Susceptibility of IN718 Casting Alloy Laser Beam Welds with a Mushroom Shape

Effect of PWHT on Microstructure and Mechanical Properties of Welded Joint of a New Fe-Ni-based Superalloy

Effect of repair welding on the fatigue behavior of AA6082-T6 T-joints in marine structures based on FFS and experiments

Effect of texture evolution and defect on the crack initiation of a Ni‐based superalloy electron beam welded joint

Controlling hot cracking in Ni-based Inconel-718 superalloy cast sheets during tungsten inert gas welding

Study on Ductility Dip Cracking Susceptibility in Filler Metal 82 During Welding

Effects of hydrogen and load frequency on the fatigue crack propagation behavior of selective laser melted Inconel 718 alloy

Welding hot cracking characteristics and fracture mechanisms of nickel‐based alloy NS1402 under different constraint conditions