The Impact of Aging Time on Fracture Mode of a Metastable Β Alloy with Network-Like Microstructure

Di Shan,Le Wang,Changqing Fang,Hui Shao,Dan Fan,Kaixuan Wang,Guo Yan

DOI: https://doi.org/10.1016/j.engfailanal.2021.105731

IF: 4

2021-01-01

Engineering Failure Analysis

Abstract:Metastable beta alloys (Ti-5Al-2Sn-2Zr-4Cr-4Mo) with network-like microstructure were obtained by aging at 630 degrees C for 1-25 h, and subjected to the tensile fracture at room temperature. The obtained alloy (equiaxed alpha and precipitated alpha phases) has the high strength and good plasticity, which are comparable to those of near-beta forged alloys. The tensile fracture mode of the short-time aging alloy is the ductile fracture with local long voids. The micro-cracks initiation at the grain boundary alpha layer and adjacent equiaxed alpha phases gives rise to the long voids. As the aging time increases up to 25 h, Al atoms penetrate within equiaxed alpha phase and Mo atoms pile up along the alpha/beta interface. During the tensile process, the release of local stress is due to the alpha/beta interface softening. The ductile fracture of the long-time aging alloy is determined by the void growth and coarsening.