High‐energy Storage Density in NaNbO3‐modified (bi0.5na0.5)tio3‐bialo3‐based Lead‐free Ceramics under Low Electric Field

Ping Peng,Hengchang Nie,Chan Zheng,Genshui Wang,Xianlin Dong
DOI: https://doi.org/10.1111/jace.17697
IF: 4.186
2021-01-01
Journal of the American Ceramic Society
Abstract:Ceramic-based dielectric capacitor are highly suitable for pulsed power applications due to their high power density and excellent reliability. However, the ultrahigh applied electric field limit their applications in integrated electronic devices. In this work, (1-x){0.96(Bi0.5Na0.5)(Ti0.995Mn0.005)O-3-0.04BiAlO(3)}-xNaNbO(3) (BNT-BA-xNN, x = 0, 0.04, 0.08, 0.12, and 0.16) ternary ceramics were designed to achieve excellent energy storage properties. It was found that the introduction of NaNbO3 (NN) effectively increase the difference (Delta P) between P-max and P-r, resulting in an obvious enhancement of the energy storage properties. High recoverable energy storage density, responsivity, and power density, that is, W-rec = 2.01 J/cm(3), xi = W-rec/E = 130.69 J/(kV.m(2)), and P-D = 25.59 MW/cm(3), accompanied with superior temperature stability were realized at x = 0.14 composition. In addition, the thermal stable dielectric properties of the sample can be prominently improved with increasing NN content. The temperature coefficient of capacitance (TCC) of x = 0.16 composition is lower than 15% over the temperature range from 49 degrees C to 340 degrees C, with a high dielectric permittivity of 1647 and a low dielectric loss (0.0107) at 150 degrees C. All these features show that the BNT-BA-xNN ceramics are promising materials for energy storage application.
What problem does this paper attempt to address?