Influence Of Heat Treatment On The Structure And Magnetic Properties Of Gd5sn4 Alloy

Xi-Chun Zhong,Hu Zhang,M. Zou,Q. Cao,Zhong-Wu Liu,De-Chang Zeng,Hong-Ya Yu,Wan-Qi Qiu,K. A. Gschneidner,V. K. Pecharsky

2010-01-01

Abstract:The Gd5Sn4 alloy was prepared by argon arc melting followed by homogenization annealing. By means of X-ray diffraction pattern and SQUID magnetometer, the effects of heat treatment on the structure and magnetic properties of Gd5Sn4 alloy were investigated. The results sho that, the uniformity of the Gd5Sn4 alloy was improved greatly after annealing at 1300 degrees C for 2h, and the Gd5Sn4 major phase increased from 85.39% in as-cast to 98.47% (molar percentage ratio) in annealed sample. The Curie temperature T-c of Gd5Sn4 alloy decreases from similar to 82K for as-cast sample to similar to 80K for annealed sample. It was also found that the homogenization heat treatment has relatively large influence on the magneticaloric effect. The maximum magnetic entropy change (-Delta S-M)(max) in a low field of Delta H=20 kOe increases from 21.5 J/kg.K to 24.65 J/kg.K after heat treatment.