Magnetic phase transition and magneto-caloric effect (MCE) in (Mn0.5Ni0.5)60+Ga40- (x = 3.3, 5.0, and 6.6) alloys
Xing Wang,Zhipan Ma,Haifeng Wang,Lingwei Li
DOI: https://doi.org/10.1016/j.jallcom.2021.160890
IF: 6.2
2021-11-01
Journal of Alloys and Compounds
Abstract:A systematic investigation of rare earth free magnets (Mn0.5Ni0.5)60+x Ga40-x (x = 3.3, 5.0, and 6.6) which are typical skyrmion hosting alloys are presented with respected to the crystal structure, magnetic phase transition and magneto-caloric effect (MCE). All the (Mn0.5Ni0.5)60+x Ga40-x alloys exhibit a hexagonal Ni2In-type structure with the P63/mmc space group confirmed by X-ray diffraction. The Mn and Ga/Ni atomic layers arrange alternately along the c-axis. The lattice parameters include a and c all as well as the Curie temperature (T C) all increase gradually with increasing Mn content. A second-ordered phase transitions from the state of ferromagnetic to paramagnetic has been determined around their own T C of 340, 348 and 351 K for (Mn0.5Ni0.5)63.3Ga36.7, (Mn0.5Ni0.5)65Ga35 and (Mn0.5Ni0.5)66.6Ga33.4, respectively. Moreover, the MCE performances of (Mn0.5Ni0.5)60+x Ga40-x alloys were determined by the figure merits of the maximum magnetic entropy change (-ΔS M max), temperature-averaged entropy change (TEC) with 5 K-lift and refrigerant capacity (RC). The values of -ΔS M max, TEC (5), and RC are 3.26 J/kg K, 3.24 J/kg K, and 229.9 J/kg for (Mn0.5Ni0.5)63.3Ga36.7, 3.72 J/kg K, 3.70 J/kg K and 287.3 J/kg for (Mn0.5Ni0.5)65Ga35, as well as 3.56 J/kg K, 3.53 J/kg K and 265.1 J/kg for (Mn0.5Ni0.5)66.6Ga33.4 under the external applied field change of 0–7 T, respectively.
materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering