Carbon Nanotubes For Property Enhancement Of Epoxy At Cryogenic Environments

Kin-Tak Lau,Hei-Lam Ma,Jinsong Leng

2015-01-01

Abstract:In the outer space, composite structures are always subject to cyclic thermal stress in which one surface of the structures facing to the Sun experiences temperature over 393 K while an opposite side is 173 K. Besides, the structures may also suffer from damages due to meteoroid attack, in which many tiny particles left over from the formation of the solar system and they are travelling at very high speed to cause serious impact and abrasion onto the structures. In the new Ares V Cargo Launch Vehicle (for the Mar's mission) designed by National Aeronautics and Space Administration (NASA), the core fuel storage tank will be made by using polymer-based composites and many materials science and engineering research have been conducted to better understand the behavior of these materials at cryogenic condition. In view of all aforementioned problems, composites used at the high attitude (at the level above the Troposphere) should be able to maintain high strength at low temperature environment. Epoxy-based composites are very popular for making advanced composites due to their high strength and chemically-inert properties, making them excellent to be used as aircraft and aerospace structural materials. However, epoxy normally behaves very brittle and therefore, loss of its toughness and impact performance at low temperature. Besides, due to their low energy dissipatability at low temperature, any impact imposed onto its structures would cause delamination and debond at an interface between reinforced fibre and matrix. Many studies have addressed that the use of single-walled (SWNTs) and multi-walled carbon (MWNTs) nanotubes could enhance the mechanical properties of polymer-based composites. However, interfacial bonding properties are always an issue as it would affect the efficiency and effectiveness of stress transfer in the composites. This paper addresses the viability of using coiled carbon nanotubes (CCNT) and randomly-oriented nanoclay-supported nanotubes (NSCNT) to enhance the mechanical properties of epoxy resin at the cryogenic environment. The results obtained from experimental fundings have shown that these nano-reinforcements could effectively enhance the property of epoxy due to their i) surface configuration which could induce the mechanical interlocking between the reinforcements and surrounding matrix and ii) the residual stress due to the shrinkage of the epoxy at low temperature environments.