Impact Of Nb Microalloying On The Hydrogen Embrittlement Of Press Hardening Steel

Jian Bian,Hardy Mohrbacher,Shiqi Zhan,Hongzhou Lu,Wenjun Wang,Yue Zhang,Li Wang
2015-01-01
Abstract:Over the last decade press hardening steel has gained strategic importance in car body manufacturing. However the alloying concept of conventional press hardening steel, 22MnB5 was originally not designed for automotive applications and consequently the specific requirements on the crash relevant material properties are not accounted for in the alloy design. One of the critical issues is delayed cracking due to hydrogen embrittlement. Previous investigations clearly demonstrated that already a very small concentration of diffusible hydrogen in press hardening steel could dramatically deteriorate steel properties like strength, elongation and toughness.This paper introduces a new metallurgical approach of improving resistance to hydrogen embrittlement of widely used press hardening steel by Nb microalloying. Samples with Nb addition from 0 to 0.08% were tested under different hydrogen charging conditions and constant load. It was found that with 0.05% Nb addition the critical fracture stress was increased by more than 2 times under the same [H] charging conditions leading to significantly higher resistance to [H] embrittlement. Hydrogen trapping and grain refinement were found to be the two dominant metallurgical effects for this achievement. Based on this investigation appropriate alloy modifications are proposed to optimize the alloying concept of 22MnB5 with the target to achieve improvement in the crash behavior of press hardened components.
What problem does this paper attempt to address?