Effect of hydrogen on deformation induced phase transformation and hot workability of Ti2AlN/Ti46Al4Nb1Mo composites
Liang Wang,Botao Jiang,Xuan Wang,Xinghong Zhang,Yingmei Tan,Hao Guo,Lijun Yang,Jiaxin Du,Ruirun Chen,Liangshun Luo,Yanqing Su
DOI: https://doi.org/10.1016/j.matchar.2024.113667
IF: 4.537
2024-02-01
Materials Characterization
Abstract:This study investigated the effect of melt hydrogenation on the as-cast microstructure, deformed microstructure evolution and deformation induced phase transformation of Ti2AlN/Ti46Al4Nb1Mo composites, and the corresponding mechanism was revealed. Results of as-cast microstructure showed hydrogen increased the length of Ti2AlN from 5 to 13 to 11–18 μm, which resulted in the decreased heterogeneous nucleation sites, thus the size of α2/γ lamellar colony increased from 27 to 33 μm. With the deforming temperature increasing from 1100 to 1200 °C and strain rates of 0.01 s−1/0.001 s−1, trace addition of hydrogen significantly reduced the peak stress and improved the hot workability. Additionally, the initial bending α2/γ lamellae decomposed, and hydrogen facilitated the lamellae decomposition as well as the phase transformation from γ to α2 phase. Hydrogen accelerated the diffusion of solute atoms and improved the mobility of dislocations, which promoted the dynamic recrystallization (DRX) of both α2 and γ phase. The enhanced atomic diffusion, especially the excess Ti atoms, reduced the barrier for the phase transformation from γ to α2 phase, and higher content of DRX for both α2 and γ phase facilitated the α2/γ lamellae decomposition. These above factors induced higher hot workability and more uniform deformed microstructure of Ti2AlN/Ti46Al4Nb1Mo composites.
materials science, multidisciplinary,metallurgy & metallurgical engineering, characterization & testing