Abstract:Carbonization of pure MnO2 by CH4-H2 gas mixture with various CH4/(CH4+H2) molar ratios in the temperature range of 900–1250°C had been performed in our previous work. This study further investigated the carbonization and alloying process of MnO2 by CH4-H2 gas mixture in the presence of Fe2O3 at 900–1300°C using XRD, optical microstructure, SEM-EDS and phase diagram analyses. Carbonization test of pure Fe2O3 was also conducted to understand the effect of Fe2O3 on the carbonization of MnO2 more explicitly. It was found that Fe2O3 could be carbonized to Fe3C at 900–1150°C. The Fe2O3 briquettes began to melt at 1100°C and a large amount of Fe-C melts appeared as the temperature went up to 1150°C. When the MnO2+25 wt%Fe2O3 briquettes were reduced at 900–1000°C in CH4-H2 gas mixture, the Fe2O3 was preferentially carbonized to Fe-C phase while the MnO2 was only reduced to MnO. The formation of Fe-C phase was beneficial to the carbonization of MnO since the carbonization temperature of MnO can decrease from 1100°C to 1000°C. The carbonization degree of MnO was dramatically accelerated over 1100°C due to the transformation of Fe-C phase from solid state to melts. Morphology analysis indicated that the MnO core was wrapped by the shell of Fe-C melts. The alloying process of Mn-Fe-C was conducted through the elements migration of Fe and Mn between the core and shell. At 1300°C, the Mn-Fe-C alloy turned to melt and aggregated since the highest melting temperature of the Mn-C-25 wt% Fe system was only 1274°C. Finally, a ferromanganese crude alloy with 68–72wt% Mn, 20–25wt% Fe and 6.0–8.0wt% C was obtained when the MnO2+25wt% Fe2O3 briquettes were carbonized by CH4-H2 gas mixture at 1300°C for 60min.

Phase Transformation Of Mno2 And Fe2o3 Briquettes Roasted Under Co-Co2 Atmospheres

A Further Investigation on the MnO2-Fe2O3 System Roasted under CO-CO2 Atmosphere

New Understanding on Separation of Mn and Fe from Ferruginous Manganese Ores by the Magnetic Reduction Roasting Process

Phase Transformations and Microstructure Evolution of Boron-Containing Iron Concentrate During Roasting under CO-CO2-N2 Atmosphere: Synergistic Effect of Soda-Ash and CO Concentration

Investigations on the MnO2-Fe2O3 System Roasted in Air Atmosphere

Systematic Study on the Synthesis and Magnetism Properties of Manganese Ferrite MnFe2O4 by an Oxidation Roasting Process

A Study on the Carbonization and Alloying Process of MnO2 by Methane-Hydrogen Gas Mixture in the Presence of Fe2O3

Green and Efficient Utilization of Ferruginous Gibbsite Ore and Ferruginous Manganese Ore by Synergetic Carbothermic Co-Reduction–Magnetic Separation Process

Phase Transformation During Roasting Process and Magnetic Beneficiation of Oolitic-Iron Ores

Preparation and Characterization of MnFe2O4 by a Microwave-Assisted Oxidative Roasting Process

Formation Mechanism of MnxFe3 − Xo4 by Solid-State Reaction of MnO2 and Fe2O3 in Air Atmosphere: Morphologies and Properties Evolution

Phase Transformations and Microstructure Evolution of Soda-Ash Roasted Boron-Containing Iron Concentrate: A Comparative Investigation of Varying Roasting Atmospheres

Separation and Recovery of Iron and Nickel from Low-Grade Laterite Nickel Ore by Microwave Carbothermic Reduction Roasting

Extraction and phase transformation of iron in fine-grained complex hematite ore by suspension magnetizing roasting and magnetic separation

Effect Of Roasting Temperature On Phase Transformation In Co-Reduction Roasting Of Nickel Slag

Precise regulation of the phase transformation for pyrolusite during the reduction roasting process

Individual enrichment of manganese and iron from complex refractory ferromanganese ore by suspension magnetization roasting and magnetic separation

Characterization Of Sulfidation Roasting Of An Iron-Rich Manganese Oxide Ore With Elemental Sulfur

Innovative Methodology for Co-Treatment of Mill Scale Scrap and Manganese Ore Via Oxidization Roasting-Magnetic Separation for Preparation of Ferrite Materials

Synergetic Utilization of Zinc-Bearing Dust by Carbothermic Reduction-Roasting Process: Phase Transformation and Morphological Evolution

Phase Transformation of High Calcium Type Tin-, Iron-Bearing Tailings During Magnetizing Roasting Process