Abstract:In this study, the diffusion bonding among YG18 cemented carbide, 30Cr2Ni2Mo alloy steel, and M4 high-speed steel was successfully realized by hot isostatic pressing. The microstructure and element diffusion of 30Cr2Ni2Mo/M4, YG18/M4, and Y18/30Cr2Ni2Mo joints were studied by electron-probe microanalysis and field emission scanning electron microscope. The mechanical properties of the three joints were evaluated by a uniaxial testing machine. The results showed that significant element diffusion occurred at the three connection interfaces. Although Kirkendall voids appeared at the 30Cr2Ni2Mo/M4 interface due to the unbalanced interdiffusion of elements, the negative effect of the Kirkendall void on the interfacial bonding strength was negligible. The η phase with a thickness of ⁓1.5 μm was formed at the YG18/M4 and Y18/30Cr2Ni2Mo interfaces. A diffusion distance of ⁓20 μm was generated at these two interfaces, where Co diffused from YG18 to M4 or 30Cr2Ni2Mo, and Fe diffused from M4 or 30Cr2Ni2Mo to YG18. The ultimate tensile strength of the 30Cr2Ni2Mo/M4, YG18/30Cr2Ni2Mo, and YG18/M4 joints was 1300.4 MPa, 736.2 MPa, and 631.2 MPa, respectively and the corresponding shear strength was 879.9 MPa, 810.0 MPa, and 360.2 MPa. The tensile and shear strength of the 30Cr2Ni2Mo/M4, Y18/30Cr2Ni2Mo, and YG18/M4 joints reached 80% of that of YG18. The tensile specimens of the 30Cr2Ni2Mo/M4 and YG18/30Cr2Ni2Mo joints failed at the M4 or YG18 side rather than at the interface, indicating that the two interfaces achieved good metallurgical bonding. The tensile specimens of the YG18/M4 joint fractured at the interface due to the existence of cracks at the YG18/M4 interface. The hot isostatic pressing enabled reliable connection among YG18, M4, and 30Cr2Ni2Mo. This study provides valuable exploitation for the reliable connection of YG18 cemented carbide and steels by hot isostatic pressing.

Study on Interface Structure and Bond Properties Between Cemented Carbide and Tool Steel Blazing with Amorphous Alloy

Microstructures and mechanical properties of YG18 cemented carbide/40Cr steel joints vacuum brazed using Ag–Cu–Ti filler metal

Influence of Brazing Technology on the Microstructure and Properties of YG20C Cemented Carbide and 16mn Steel Joints

Effects of Bonding Temperature on Mechanical Properties and Interfacial Morphology of YG8/40Cr Joints Fabricated Using SPS Diffusion Bonding

Experimental Study and Computer Simulation on Multicomponent Diffusion in Multiphase Dispersions During Solid Carburizing of HP40Nb and KHR45A Alloys

Optimisation of sintering parameters for bonding nanocrystalline cemented tungsten carbide powder and solid high strength steel

Study on Effect of High-Entropy Alloy Binder on Microstructure and Properties of WC Cemented Carbide Doped with Rare Earth Oxide

Microstructure and mechanical properties of cemented carbide to steel joints by electron beam welding

The Preparation Process, Microstructure and Properties of Cellular TiC-High Mn Steel-Bonded Carbide

Microstructural evolution and mechanical properties of Ni-based superalloy joints brazed using a ternary Ni-W-B amorphous brazing filler metal

Microstructures and Properties of WC-10 wt.%CoCrFeNiAlx Composite Cemented Carbides

Effect of Alloy Carbides on Structure and Properties of Shearing Blade Steel HM

Effect of Cu Ce Alloy Addition on the Microstructure and Mechanical Performance of Brazed Diamonds with Ni Cr Alloy

Microstructural Evolution and Mechanical Properties of Ti2AlNb/GH99 Superalloy Brazed Joints Using TiZrCuNi Amorphous Filler Alloy

Microstructure and properties of coarse WC-10CoCrFeMnNi cemented carbide by mechanical alloying and hot pressing sintering

Diffusion Brazing of GH536 Polycrystalline Superalloy with IC10 Single Crystal Superalloy Using BNi-2 Interlayer

Diffusion bonding among hard alloy, tool steel, and alloy steel by hot isostatic pressing: Interfacial microstructure and mechanical properties

Microstructure and properties of a YG18/40Cr joint vacuum–brazed by Cu–Sn–Ti filler metal

Coarse Grained Heat-Affected Zone Microstructure and Brittleness of Ti-Nb-B Microalloyed High Toughness and Wear Resistant Steel

Interfacial Microstructure and Properties of TiC Cermet and GH3128 Joint Brazed Using AgCuNiLi

Effect of Carbides on Thermos-Plastic and Crack Initiation and Expansion of High-Carbon Chromium-Bearing Steel Castings