Abstract:The phase equilibrium of Mg-Cu-Ca ternary system at 350 degrees C were investigated using thirteen key samples. Scanning electron microscopy (SEM) equipped with energy-dispersive spectroscope (EDS) was employed to investigate equilibrium relationships and phase compositions in alloy samples. Powder X-ray diffraction (XRD) technique was used to analyze the crystal structures of new found phases. Two unreported ternary phases, P1 and Mg25-xCu75Cax were observed and investigated for the first time. The compound P1 has a narrow solid homogeneity ranged from about Mg25Cu35Ca40 to Mg30Cu30Ca40 (in at. %). The solid solubility limit of the compound Mg25-xCu75Cax was found to be 8.03 <= x(Ca) <= 16.67 with constant value of about 75 at. % Cu at 350 degrees C. The 2q of fourteen diffraction peaks of new phase P1 were determined to be 23.0 degrees, 35.9 degrees, 37.3 degrees, 38.9 degrees, 42 degrees, 44 degrees, 47 degrees, 52.5 degrees, 54 degrees, 56.7 degrees, 62.3 degrees, 66.8 degrees, 68.2 degrees and 75.4 degrees. The 2q of ten diffraction peaks of the new compound Mg25-xCu75Cax were confirmed to be 20.5 degrees, 21.2 degrees, 34.7 degrees, 35.7 degrees, 42.3 degrees, 43.3 degrees, 44.8 degrees, 47.3 degrees, 50.5 degrees and 74.5 degrees. The maximum solid solubility of Ca in the terminal compound MgCu2 was found to be 8.83 at. % at 350 degrees C. Ternary maximum solid solubility of binary terminal compounds Mg2Ca, Mg2Cu, Cu5Ca and CuCa were less than 2 at. %. In addition, eight three-phase equilibrium relationships were determined in the present work. (C) 2019 Elsevier B.V. All rights reserved.

Phase Equilibria of the Al–Zn–Fe–V Quaternary System at 620 °C

Phase Equilibria In The Fe-Nb-Zr Ternary System At 1,200 A Degrees C

Phase equilibria in the Fe-Ti-Zr system at 1023 K

Phase equilibria in the Fe–Nb–Zr ternary system at 1,200 °C

Phase Relationships in the Al-rich Region of the Al-Y-Zr System

Thermodynamic calculation of phase equilibria in the Al–Fe–Zn–O system

Experimental study of the phase relations in the Fe–Cr–Si ternary system at 700°C

Experimental Investigation and Thermodynamic Assessment of Phase Equilibria in the Al-Ta-V Ternary System

Phase equilibria in Co−Al−Re ternary system at 1100 and 1300 °C

Measurement of the phase equilibria in the Al–Zr–Y system at 673 and 823 K

Phase relationship of the Ag–Zr–Cr system at 1000 and 750°C

Experimental Determination of the Phase Equilibrium in the Mg–Cu–Ca Ternary System at 350 °C

Phase Equilibria of the Sn–Zn–Cu Ternary System

Solidification paths and phase equilibria at 873 and 673 K in the Al-Er-Zr system

Phase Equilibria in the Al–Co–Cr–Fe–Ni High Entropy Alloy System: Thermodynamic Description and Experimental Study

Experimental Investigation of Phase Equilibria in the Fe-Nb-Ta System

Experimental determination of phase diagram in the Zn-Fe binary system

Phase Equilibria of the Fe–Nb–Ti System at 900 °C

Thermal stability of Al–Fe–Ni alloy at high temperatures

Thermodynamic description of the Al–Ag–Zr system and discovery of the high-strength ternary phase Al1.84Ag0.16Zr

Solidification Paths and Phase Components at High Temperatures of High-Zn Al-Zn-Mg-Cu Alloys with Different Mg and Cu Contents