Abstract:Poly (vinyl alcohol)/layered double hydroxide (PVA/LDH) composite films with different LDH contents have been fabricated through casting with an in situ hydrothermal treatment. Wide angle X-ray diffraction WAXD) results show the characteristic (003) diffraction reflection peak of LDH layers and the corresponding peak becomes stronger with the increase of LDH content, and the size of LDH layers can be tuned by the concentration of reactant. Lower reactant concentration leads to small size of LDH particles while higher concentration gives LDH particles with large size. LDH particles are homogeneously dispersed in PVA matrix as evidenced by SEM observations. The tensile strength and the elastic modulus of PVA films are improved by introducing LDH particles. With the LDH content of 1. 0 wt%, the tensile strength and elastic modulus of the corresponding composite films are improved by about 105. 4% and 133. 2%, respectively, compared with those of a neat PVA film. It is believed that most OH groups of PVA undergo interfacial H-bonding with the LDH layers and other PVA chains,which might be account for the improvement of mechanical properties. Interesting thing is that the in situ PVA/LDH composite aqueous solution shows lower viscosity than that of PVA aqueous solution and the viscosity decreases with LDH content, which is in strong contrast to that by traditional simple mixing. LDH layers are considered to shield the entanglement of PVA chains and thus lead to decreasing solution viscosity. Furthermore, the anti-absorbent of water for the composite films are also improved without losing transparency, while the improvement of gas barrier cannot be observed until the loading of LDH reaches to 3. 0 wt%.

Tunable Properties of Exfoliated Polyvinylalcohol Nanocomposites by in Situ Coprecipitation of Layered Double Hydroxides

Poly(L-Lactide)/Layered Double Hydroxides Nanocomposites: Preparation and Crystallization Behavior

Preparation And Characterization Of Poly(Vinyl Chloride)/Layered Double Hydroxides Nanocomposite Via In Situ Suspension Polymerization

Preparation and characterization of poly(vinyl chloride)/layered double hydroxides nanocomposite viain situ suspension polymerization

Tailoring the Performance of Polymer Composites Via Altering the Properties of the Intrapore Polymers of MCM-48 Nanocomposites As Fillers

Fabrication of High-Performance Poly(Vinyl Alcohol)/Mgal-Layered Double Hydroxide Nanocomposites

Preparation of the poly(vinyl alcohol)/layered double hydroxide nanocomposite

Facile Synthesis of LDH Nanoplates As Reinforcing Agents in PVA Nanocomposites

Preparation of Poly(Methylmethacrylate)/Layered Double Hydroxides Nanocomposites Via in Situ Solution Polymerization

Studies on Poly (vinyl alcohol)/Layered Double Hydroxide in situ Composite Films

Improvement of optical, dielectric and mechanical properties of a new nanocomposite based on polyvinyl alcohol and layered double hydroxide

Synthesis and modification of the structural, optical, and thermal properties of PVA–PEO by LDH nanoplates

Nanoscale Dispersion of Delaminated Sheets of Layered Double Hydroxides in Polyvinyl Acetate

Microstructure and Thermal and Tensile Properties of Poly(vinyl Alcohol) Nanocomposite Films Reinforced by Polyacrylamide Grafted Cellulose Nanocrystals

PREPARATION AND CHARACTERIZATION OF VINYLIDENE CHLORIDE COPOLYMER/LAYERED DOUBLE HYDROXIDES NANOCOMPOSITES

Structural characterization and related properties of EVA/ZnAl-LDH nanocomposites prepared by melt and solution intercalation

Synthesis of Exfoliated Pp/Ldh Nanocomposites Via Melt-Intercalation: Structure, Thermal Properties, and Photo-Oxidative Behavior in Comparison with Pp/Mmt Nanocomposites

A novel approach for preparing exfoliated UV-cured polymer/LDH nanocomposites via pre-exfoliated organic LDH

Structural characterization, thermal and mechanical properties of polyurethane/CoAl layered double hydroxide nanocomposites prepared via in situ polymerization

Phosphorylated Cellulose Applied for the Exfoliation of LDH: an Advanced Reinforcement for Polyvinyl Alcohol

Preparation and Properties of UV-curable Organic / Inorganic Hybrid Nanocomposites Based on Layered Double Hydroxides