Abstract:： In order to investigate the effects of stress triaxiality, Lode angle, temperature and strain rate on the fracture characteristics of 6061-T651 aluminum alloy materials, the mechanical property tests of materials are carried under different stress states, temperature and strain rate using universal material testing machine. Firstly, the mechanical property test results show that the fracture strain of 6061-T651 aluminum alloy material decreases with the increase of stress triaxiality. And also, the fracture strain of material related to the Lode angle parameter, especially the effect of the Lode angle more significantly at the range of lower stress triaxiality. When the temperature less than 250 ℃ , the temperature of material has significant influence on its flow stress, while the influence of temperature on its fracture strain can be ignored. While the temperature more than 250 ℃ , the temperature of material has greatly influence on its flow stress and fracture strain. Moreover, the strain rate has no significant effect on the fracture strain of 6061-T651 aluminum alloy. Subsequently, basing on the test results of mechanical properties, the Modified Johnson-Cook(MJC) criterion is obtained by modifying Johnson-Cook(J-C) fracture criterion, and the parameters of MJC and Modified Mohr-Coulomb(MMC) fracture criterion are calibrated. Finally, the impact test of sphere projectile penetrating the 6061-T651 aluminum alloy target plate is conducted on a one-stage gas gun, and also the ballistic limit velocity and failure mode of target are obtained. In order to verify the validity of the model and parameters, and the corresponding 3D model of projectile impact target is established by using ABAQUS/Explicit finite element software. The results showed that the prediction results of Lode angle dependent MMC fracture criterion is closer to the test compared with the Lode angle independent MJC fracture criterion.

Experimental And Numerical Investigation Of Aluminum Alloy Plates With Initial Crack Under Repeated Dynamic Impact Loads

Numerical Study of CFRP-Bonded Pressure Pipes Subject to Impact Load

DAMAGE ACCUMULATION, FRACTURE AND POST FRACTURE ANALYSES FOR INITIALLY FLAWED STEEL STRUCTURES

The experimental and numerical study of AA6061-T6 aluminum alloy under repeated impacts

Characterization of the Fracture of an Aluminum Alloy Anticollision-Beam to Impact Loading

Experimental and numerical study of residual ultimate strength of hull plate subjected to coupled damage of pitting corrosion and crack

Numerical Investigation on Polyurea Coated Aluminum Plate Subjected to Low Velocity Impact

Numerical Analysis of Experiments on Damage and Fracture Behavior of Differently Preloaded Aluminum Alloy Specimens

Nonlinear analysis model of the progressive damage of aluminum–wood sandwich structures under high-speed impact conditions

Deformation response research on aluminum sheets with different central pre-cracked defects under quasi-static hydraulic pressure loading

Experimental and numerical investigation on plasticity and fracture behaviors of aluminum alloy 6061-T6 extrusions

Study of dynamic mechanical behavior of 1060-H112 aluminum alloy: Experimental and numerical simulation

Analysis of ductile damage and fracture under reverse loading

Damage-Accumulation-Induced Crack Propagation and Fatigue Life Analysis of a Porous LY12 Aluminum Alloy Plate

Practical Formula for Predicting the Residual Deflection Evolution of Steel Plates Subjected to Repeated Impacts

Experimental and numerical investigations into the ductile fracture during the forming of flat-rolled 5083-O aluminum alloy sheet

Dynamic Mechanical Properties and Modification of Fracture Criteria of 6061-T651 Aluminum Alloy

Numerical simulation of dynamic impact spall of ultra high strength 7055 aluminum alloy

A Study on Crack Initiation and Propagation of Welded Joints under Explosive Load

Experimental and numerical study of water-filled vessel impacted by flat projectiles

Simulation and Experimental Investigation of Multi-Step Shot Peening for Surface Crack Repair in Aluminum Alloys