The Preparation and Property of Magnetic Chitosan Membrane
TANG Shan-gang,YUAN Xia,LIANG Da-xing,LIU Xing-yun,JIANG Lin-bin,LIAO Dan-kui
DOI: https://doi.org/10.3969/j.issn.1001-7445.2014.03.011
2014-01-01
Abstract:In order to study the local drugs release of target of drug material which was loaded by ch-itosan membrane, chitosan and Fe3 O4 were used as material, and curtain coating method was used to prepare the magnetic composite membrane of chitosan. The swelling property, moisture permeation property, mechanical property, acid resistance, mangnetic responsiveness of magnetic membrane were tested. Its structure was characterized by Fourier Transform Infrared Spectroscopy ( FTIR ) and X-Ray Diffraction (XRD). Experimental results showed that after adding Fe3O4, the mois-ture-penetrability and swelling property of the magnetic composite membrane became weaker;swelling degree was decreased from 173% to 91%; moisture coefficient was decreased from 6.7í10-8 g/(h·mm·Pa) to 5. 1í10-9 g/(h·mm·Pa) but tensile strength was increased from 4.6 MPa to 5.8 M Pa, and acid resistance was also increased. Vibrating Sample Magnetometer ( VSM) test indicated that the composite membrane was with magnetism, and the higher of the con-tent of Fe3 O4 , the stronger of magnetism. FTIR and XRD tests proved that Fe3 O4 was contained in the membrane.