Improved water-splitting performances of CuW 1− x Mo x O 4 photoanodes synthesized by spray pyrolysis

Qing Liang,Yongsheng Guo,Ningsi Zhang,Qinfeng Qian,Yingfei Hu,Jianqiang Hu,Zhaosheng Li,Zhigang Zou

DOI: https://doi.org/10.1007/s40843-018-9287-5

2018-01-01

Abstract:CuW 1− x Mo x O 4 solid solution of CuWO 4 and CuMoO 4 , which is a copper-based multi-component oxide semiconductor, possesses much narrower band gap than CuWO 4 . In theory, it can absorb a larger part of the visible spectrum, widening the use of solar spectroscopy and obtaining a higher photo-to-chemical conversion efficiency. In this study, CuW 1− x Mo x O 4 thin-film photoanodes on conducting glass were prepared using a simple and low-cost spray pyrolysis method. The resulting CuW 1− x Mo x O 4 photoanodes perform higher photocurrent than CuWO 4 photoanodes under AM 1.5G simulated sunlight illumination (100 mW cm −2 ) in 0.1 mol L −1 phosphate buffer at pH 7. Combined with IPCE and Mott-Schottky analysis, the enhancement of the photocurrent is due to the improvement of photon utilization and the increase of carrier concentration with the incorporation of Mo atoms. Moreover, with the optimal Mo/W atomic ratio, the photocurrent density increases obviously from 0.07 to 0.46 mA cm −2 at 1.23 V RHE bias. In addition, compared with particle-assembled thin-film photoanodes prepared by solidphase reaction and drop-necking treatment, the photoanodes prepared by spray pyrolysis have obvious advantages in terms of reducing resistance and facilitating charge transport.