Study on the Interaction Between the Active Phase and Support on V2O5/TiO2 Catalyst

Ye Daiqi,Liang Hong,Huang Zhongtao
DOI: https://doi.org/10.3866/pku.whxb19930415
1993-01-01
Abstract:V2O5 supported on various TiO2 including anatase, ratile and mixture of both types have been investigated with varicus physicochemical measurements such as BET, TPD, NARP, XRD and so on. It has been found that the V=O species or the (010) plane of V2O5 on all the TiO2 supports with large BET surface area are selectively exposed to the surface, though different modification of TiO2 results in different characteristics of exposure of (010) plane. For anatase, the maximum exposure of the V=O species is obtained at the surface concentration of V2O5 significantly lower than that for rutile. For the mixture, two maxima are obtained in the surface concentration of V2O5 corresponding to those for anatase and rutile respectively. Thus, it is concluded that crystal structure of the TiO2 support determines the maximum exposure of (010) plane. The chemical activity of TiO2 surface also seems to have an effect on the exposure of (010) plane. That is, the higher surface area and the stronger acidic property resulted in the high exposure of (010) plane.
What problem does this paper attempt to address?