Anticorrosive Properties Of Styrene-Acrylic Resins Containing Aluminum Tripolyphosphate
Lin-Jian Shangguan,Wugang Ma,Guoqin Liu,Weiqiang Song
2015-01-01
Abstract:Corresponding author: Guoqin LIU – Ph.D., Eng, Associate Professor, e-mail: liugq1970@126.com Introduction Emulsion polymerization is widely used to produce water-based resins with various colloidal and physicochemical properties [1 – 4]; the reaction medium is usually water, which facilitates agitation and mass transfer, and provides an inherently safe process; moreover the process is environmentally friendly. Styrene acrylic emulsion is widely applied in the area of coating and adhesive for its prominent properties such as good durability, availability at low cost, compatibility with other materials, excellent adhesive characteristic, and ability to form continuous film upon drying of the emulsions, high resistance to UV light, oxygen, water, various types of solvents and excellent durability [5, 6]. However, styrene-acrylic emulsion-based polymer provides little anticorrosion property. It seems reasonable to prepare styrene acrylic emulsionbased composites for building anticorrosion materials by incorporating anticorrosion pigment. Traditional anticorrosive paints contain lead or chromium compounds as active pigments; however, these pigments lead to the environmental pollution and, meanwhile, pose a risk to human health. One of the leading substitutes for these classic pigments is the inorganic tripolyphosphate, which constitutes a promising group of nontoxic phosphate corrosion inhibitors for paints. Among them, aluminum tripolyphosphate (AlH2P3O10·2H2O: ALP) has been developed and used widely as an anticorrosion pigment due to its low toxicity to humans and environment, and better anticorrosive properties. In this study, we synthesised a styrene-acrylic emulsion composite with ALP for anticorrosion resins. The structural characteristics, distribution and particles size and anticorrosion performance of styrene-acrylic resins/aluminum tripolyphosphate coatings were investigated. In addition, to study the effect of ALP on final properties of coatings, the coatings with no pigment (blank coating), calcium tripolyphosphate (Ca5(P3O10)2: CAP) and zinc phosphate (Zn3(PO4)2: ZNP) were employed as references.