Abstract:Aluminum alloys are extensively used in many fields such as aeronautics, astronautics, vehicle manufactures and living products clue to their good mechanical properties and anti-corrosion performance. Traditionally, the most effective corrosion protection technologies are based on the use of Cr6+ containing formulations to extend the applications of aluminum alloys in high corrosive media such as chlorides containing solutions. However, the recent recognition that chromates are highly toxic and carcinogenic has led to extensive research to develop new alternatives. Many works have been published using different conditions to obtain rare earth (RE) conversion layers on several aluminum substrates. Unfortunately, these reported anti-corrosion technologies based on RE modified films presented several drawbacks including long formation time, high formation temperature and even high potential in some cases. The goal of the present work is to introduce the novel cathode electrophoresis technique to quickly deposit cerium modified film on the surface of Al 5083. The morphology and structure of the RE. film were characterized by SEM, EDS and XRD, the corrosion resistance was investigated by EIS and potentiodynamic polarization curves in 0.1 mol/L NaCl solution. The results showed that uniform CeO2 film of 0.8 mu m thickness can be prepared by cathode electrophoresis process in 0.1 mol/L Ce(NO3)(3) ethanol solution at a voltage of 12 V for 60 s. Polarization curves confirmed its excellent protective property through inhibiting the cathodic reaction. Impedance data collected from EIS in 0.1 mol/L NaCl solution remained capacitive for 31 d, which indicated the lack of localized corrosion. With the increase of exposure time, the charge-transfer resistance R-p became higher, the surface capacitance C-t nearly kept constant and cracks of the film reduced obviously, demonstrating a self-healing property. Apparently local cathodes were covered during the RE modification processes, thereby reducing the driving force for pitting.

Corrosion Protective Behavior of Typical Inhibitor Pigments on Aluminum Alloy Used for Transportation

Cerium Cinnamate As an Environmentally Benign Inhibitor Pigment for Epoxy Coatings on AA 2024-T3

Cerium Tartrate As A Pigment in Epoxy Coatings for Corrosion Protection of Aa 2024-T3

Corrosion Electrochemical Characteristics of Red Iron Oxide Pigmented Epoxy Coatings on Aluminum Alloys

Corrosion resistance of anodically oxidized LY12 aluminum alloy after modification with cerium nitrate and silane

Anticorrosion Properties of Composite Inhibiting Pigment Based on Natural Calcium Silicate and Zinc Monophosphate

Synthesis and characterization of modified iron oxide hydrophobic corrosion-resistant pigment for aluminum alloy coating

Electrochemical Study of Corrosion Behavior of Rare Earth Based Chemical Conversion Coating on Aerospace Aluminum Alloy

Corrosion Resistance of P2 Inhibitor Treatment of Aluminum Alloy

Fabrication and characterization of corrosion resistant vinyl sulfone reactive dye-encapsulated colored aluminum pigment composites

Corrosion Protection Of Aluminium Alloy 2024-T3 In 0.05 M Nacl By Cerium Cinnamate

Catechol/m-Phenylenediamine Modified Sol–Gel Coating with Enhanced Long-Lasting Anticorrosion Performance on 3003 Al Alloy

Inhibition of the Corrosion of Aluminum Alloy by a Composition of Ion-Exchange Pigments

Characterization and Cathode Electrophoresis Deposition of Cerium Modified Films on Al 5083

Degradation of Typical Protective Coatings on Al-Alloy Used for Transportation in High-temperature and High-humidity Region

Study on the Influence of Surface Treatment Process on the Corrosion Resistance of Aluminum Alloy Profile Coating

Electrochemical corrosion resistance of aluminum alloy 6101 with cerium-based coatings in an alkaline environment

Study of Corrosion Inhibition of Coupled Al2Cu–Al and Al3Fe–Al by Cerium Cinnamate Using Scanning Vibrating Electrode Technique and Scanning Ion-Selective Electrode Technique

Corrosion inhibition analysis on cerium induced hydrophobic surface of Al-6061/SiC/Al2O3 hybrid composites

The Research Advance of Preparation and Modification of Aluminum Tripolyphosphate

Hydrothermal and cerium salt sealing of a 6061 aluminum alloy