Research Progress and Prospect of Acoustic Emission Technology in failure Mechanism of Thermal Barrier Coatings
Zhijun Cao,Jianhui Yuan,Huaiyu Su,Jiabao Wan,Jiahui Su,Qian Wu,Liang Wang
DOI: https://doi.org/10.11933/j.issn.1007?9289.20220728001
2023-01-01
China surface engineering
Abstract:Thermal barrier coatings (TBCs) have attracted much attention because of their excellent high-temperature oxidation resistance and high-temperature mechanical and hot corrosion resistance. They are widely used in aero-engine and gas turbine hot-end components. Owing to the poor service environment and complex structure of TBCs, elastic-plastic deformation of the substrate, surface cracks, and interface cracks easily occur, leading to interface delamination or spalling failure. To understand the crack initiation and propagation in TBCs further, it is important to predict the cracking, delamination time, delamination or failure location, and damage mode of TBCs accurately. In this study, the principles of photo-stimulated luminescence piezo spectroscopy, infrared thermography, and impedance spectroscopy, as well as their applications in the study of the failure behavior of TBCs, are briefly reviewed, with emphasis on the application of acoustic emission (AE) technology as an important nondestructive testing method in the study of the failure behavior of TBCs. The research achievements of scholars worldwide in exploring the failure mechanisms of TBCs under tension, compression, three-point bending, high-temperature thermal shock, thermal shock, etc. are summarized. Based on the signal analysis and deep processing of the failure process of TBCs, the characteristics of AE signals are represented by waveform characteristic parameters (such as amplitude, energy, count, duration, rise time, peak frequency, and center frequency). Combined with parameter analysis and waveform analysis of AE technology in TBCs, the failure process and failure patterns of the TBCs are recognized based on AE signals. The service life of TBCs is predicted by a quantitative evaluation of the degree of damage. These results can provide a reference for the development of an AE monitoring platform for TBCs and promote the development of engineering applications. Although significant progress has been made in analyzing the degradation behavior and reliability of TBC systems in recent years, some shortcomings in the ability to predict damage evolution in terms of crack initiation and propagation remain. AE can be used for permanent structural-health monitoring of TBCs. For the damage evolution of microcracks and pores, adverse changes in the structure are detected and explained to improve reliability, and the elastic waves carrying the information about defects and potential defects are analyzed. In summary, AE technology plays an important role in the characterization, service status, and life prediction of TBCs. It is also an effective auxiliary method in the failure research of TBCs. Machine learning is a subset of artificial intelligence, and the application of nondestructive testing technology in TBCs using machine-learning methods is briefly described. Methods to realize intelligent recognition and life prediction of machine learning in TBCs based on AE technology are discussed. These research results not only enrich the understanding of AE technology but also indicate the direction for failure prediction and life assessment of TBCs. Finally, a future AE technology research trend in the fatigue damage of TBCs is proposed.