Carbon skeleton materials derived from rare earth phthalocyanines MPcs (M=Yb, La) used as high performance anode materials for lithium-ion batteries

Tingting Jiang,Mihong Cao,Jun Chen,Luyi Wang,Qian Zhang,Hua Wang,Jintian Luo

DOI: https://doi.org/10.1039/d3dt00505d

IF: 4

2023-04-16

Dalton Transactions

Abstract:In this work, novel carbon skeleton materials were prepared by high-temperature carbonization of rare earth phthalocyanines MPcs (M=Yb, La) in nitrogen atmosphere. The resulting carbon material of YbPc-900 (carbonisation temperature of 900 °C for 2 h) and LaPc-1000 (carbonization temperature of 1000 °C for 2 h) have a graphite-layered structure in predominantly ordered states, which have a smaller particle size, a larger specific surface area and a higher degree of hard carbonization compared to the uncarbonized sample. As a result, the batteries using YbPc-900 and LaPc-1000 carbon skeleton materials as electrodes display excellent energy storage behaviors. The initial capacities of YbPc-900 and LaPc-1000 electrodes at 0.05 A/g were 1100 and 850 mAh/g , respectively. After 245 cycles and 223 cycles, the capacities remain at 780 and 716 mAh/g with retention ratio of 71 % and 84%. At high rate of 1.0 A/g, the initial capacities of YbPc-900 and LaPc-1000 electrodes were 400 and 520 mAh/g , respectively, and after 300 cycles, the capacities can still remain at 526 and 587mAh/g with retention ratio of 131.5 % and 112.8 %, respectively, which were much higher that the pristine rare earth phthalocyanines MPcs (M=Yb, La) electrodes. Moreover, better rate capability were also observed during the YbPc-900 and LaPc-1000 electrodes tests. The capacities of the YbPc-900 electrode at 0.05, 0.1, 0.2, 0.5, 1 and 2C were 520, 450, 407, 350, 300 and 260 mAh/g respectively, which were higher than that of the YbPc electrode (550, 450, 330, 150, 90 and 40 mAh/g). Similarly, the rate performance of LaPc-1000 electrode at different rates were also significantly improved compared to that of pristine LaPc electrode. In adddition, the initial coulomb efficiencies of YbPc-900 and LaPc-1000 electrodes were also greatly improved than those of pristine YbPc and LaPc electrodes. After carbonization, the YbPc-900 and LaPc-1000 carbon skeleton materials derived from rare earth phthalocyanines MPcs (M=Yb, La) present improved energy storage behaviors, which would provide new ideas for developing novel organic carbon skeleton negative materials for lithium ion batteries.

chemistry, inorganic & nuclear