High electric energy and power density achieved in P b 1 − x L a x [ ( Z r 0.55 S n 0.45 ) 0.92 T i 0.08 ] 1 − x ∕ 4 O 3 antiferroelectric ceramics by La dopants
Qingshan Zhu,Kai Zhao,Ran Xu,Yujun Feng,Zhuo Xu,Xiaoyong Wei
DOI: https://doi.org/10.1016/j.jallcom.2021.160108
IF: 6.2
2021-10-01
Journal of Alloys and Compounds
Abstract:<p>In order to improve the energy storage and discharge performance of ceramic dielectric capacitors, antiferroelectric materials have drawn wide attention. In this work, a comprehensive investigation on <span class="math"><math>Pb1−xLax[(Zr0.55Sn0.45)0.92Ti0.08]1−x∕4O3</math></span> (x = 0%, 2%, 4%, 6%) antiferroelectric ceramics are fabricated by a rolling process. With the addition of lanthanum(La), the average grain size and the electric-field-induced strain are suppressed. However, the energy conversion efficiency, particularly the efficiency of −60 °C, is enhanced with increasing La content. In addition, the released energy density calculated by the "quasi-static" method(<em>W</em><sub><em>re</em></sub>) and "dynamic" method(<em>W</em><sub><em>dis</em></sub>) were investigated comparatively. As the content of La increase, the discrepancy between<em>W</em><sub><em>re</em></sub> and<em>W</em><sub><em>dis</em></sub> gradually decreased. Specifically, the composition with 4%La doped has the best comprehensive performance, with the highest recoverable energy density of 5.61 J/cm<sup>3</sup> and ultrahigh efficiency of 90% at 410 kV/cm. Moreover, a discharge energy density of 3.6 J/cm<sup>3</sup> can be obtained at 222 kV/cm and 90% can be released in 0.68<em>μ</em>s. By directly short experiment, a current density of 1599A/cm<sup>2</sup> and power density of 177 MW∕cm<sup>3</sup> were obtained. These results indicated that PLZST 4/55/45/8 is promising for high electric energy and power density capacitors.</p>
materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering