V2O5 Nanosheets/Reduced Graphene Oxide Nanocomposite As a High-Performance Cathode Material for Lithium-Ion Batteries
Jianli Cheng,Bin Wang
DOI: https://doi.org/10.1149/ma2014-04/2/407
2014-01-01
Abstract:Among the existing cathode materials, V 2 O 5 is a promising cathode candidate because of its high energy density, abundance, easy synthesis, as well as low cost. However, due to quite low diffusion coefficient of lithium ions (10 -12 -10 -13 cm 2 s -1 ), irreversible phase transitions during deep discharge, and vanadium dissolution into the electrolyte, the practical use of V 2 O 5 as a cathode material shows poor rate capability and cycling stability 1,2 . Incorporating the nanostructured V 2 O 5 with high conductive materials to build a hybrid material is one of the most promising strategies to improve the electrochemical property of the V 2 O 5 based anod 3 . Among these conductive materials, graphene nanosheet (GNS), with the exceptional properties of excellent electronic conductivity of 10 3 -10 4 S m -1 , high theoretical surface area of 2630 m 2 g -1 , and high mechanical flexibility is much more attractive. Extensive studies of GNS-V 2 O 5 nanocomposites have been investigated. However, it is worth noting that most of the reported nanocomposites constitute by the GNS with the zero-dimensional (0-D) nanoparticles or one-dimensional (1-D) V 2 O 5 nanofiber/nanorod. To the best of our knowledge, the 3-D nanocomposites combining the GNS layer with 2-D V 2 O 5 nanosheets have not been reported so far. Herein, we demonstrate a simple solvothermal method to directly self-assemble 2-D V 2 O 5 nanosheets on the reduced graphene oxide, forming 3-D nanocomposite (V 2 O 5 nanosheet/RGO hierarchical nanocomposite). Briefly, vanadium oxytriisopropoxide (VO(OiPr) 3 ) and graphene oxide (GO) were dispersed into ethyl alcohol by ultrasonicaiton to produce a V-precursor/GO dispersion. Then, the dispersion was transferred to a Teflon-lined stainless steel autoclave and heat-treated in an electric oven. The obtained composite was further annealed at 300°C in air to make V 2 O 5 crystallized and reduce GO to RGO. The detailed preparation procedures can be found in the experimental section. When used as a cathode material, the V 2 O 5 nanosheets/RGO nanocomposites exhibits highly reversible capacity and good rate capability over bulk material. The V 2 O 5 nanosheets/RGO nanocomposite anode was able to charge/discharge at high current densities of 15A g -1 (50C), with the discharge capacities of approximately 176 mA h g -1 . Meanwhile, a discharge capacity of 102 mA h g -1 can be delivered after 160 cycles at 2C, showing a good cycling stability. The improved performance could be attributed to the enhanced electron transport and Li + diffusion that result from the hierarchical nanostructure of V 2 O 5 nanosheets/RGO nanocomposite (showing in Figure 1). Reference: [1] S. Q. Wang, S. R. Li, Y. Sun, X. Y. Feng, C. H. Chen, Energy & Environmental Science 2011, 4, 2854. [2] Y. X. Tang, X. H. Rui, Y. Y. Zhang, T. M. Lim, Z. L. Dong, H. H. Hng, X. D. Chen, Q. Y. Yan, Z. Chen, Journal of Materials Chemistry A 2013, 1, 82. [3] X. H. Rui, J. X. Zhu, D. Sim, C. Xu, Y. Zeng, H. H. Hng, T. M. Lim, Q. Y. Yan, Nanoscale 2011, 3, 4752.