Synergistic effects of niobium oxide–niobium carbide–reduced graphene oxide modified electrode for vanadium redox flow battery
Ting-Ruei Liu,Yu-Chung Chang,Anteneh Wodaje Bayeh,Kai-Chin Wang,Hsueh-Yu Chen,Yao-Ming Wang,Tai-Chin Chiang,Mau-Tsu Tang,Shao-Chin Tseng,Hsin-Chih Huang,Chen-Hao Wang
DOI: https://doi.org/10.1016/j.jpowsour.2020.228590
IF: 9.2
2020-10-01
Journal of Power Sources
Abstract:<p>A powerful, low-cost niobium oxide–niobium carbide–graphene oxide (NbO<sub>2</sub>/NbC/rGO) hybrid electrocatalyst is prepared by refluxing, hydrothermal method, followed by annealing process at the optimum temperature of 1050 °C for all vanadium redox flow battery (VRFB) application. The NbO<sub>2</sub>/NbC/rGO electrocatalyst shows the best electrochemical activity with the highest peak current densities and the lowest peak differences toward VO<sub>2</sub><sup>+</sup>/VO<sup>2+</sup> and V<sup>2+</sup>/V<sup>3+</sup> redox reactions from the cyclic voltammetry compared to other samples. The rate performance of VRFB cell using NbO<sub>2</sub>/NbC/rGO modified graphite felts (NbO<sub>2</sub>/NbC/rGO/GF) shows the voltage efficiencies of 89.3%, 81.7%, 71.0%, and 59.3% by the charge-discharge current densities of 40 mA cm<sup>−2</sup>, 80 mA cm<sup>−2</sup>, 120 mA cm<sup>−2</sup>, and 160 mA cm<sup>−2</sup>, respectively, which these performances are superior to those using the pretreated GFs and the untreated GF. The charge-discharge stability test of the VRFB cell using NbO<sub>2</sub>/NbC/rGO/GF demonstrates no significant decay after 100 cycles by the current density of 80 mA cm<sup>−2</sup>. This observation is due to the synergistic effects related to the presence of excess oxygen vacancies on NbO<sub>2</sub>/NbC, the high content of oxygen functional groups, and the high electrical conductivity characteristics of the graphene sheet.</p>
energy & fuels,materials science, multidisciplinary,electrochemistry,chemistry, physical