Laser Powder Bed Fusion of High-Strength Sc/Zr-modified Al–Mg Alloy:Phase Selection, Microstructural/mechanical Heterogeneity, and Tensile Deformation Behavior

Zihong Wang,Xin Lin,Nan Kang,Jing Chen,Hua Tan,Zhe Feng,Zehao Qin,Haiou Yang,Weidong Huang
DOI: https://doi.org/10.1016/j.jmst.2021.03.069
2021-01-01
Journal of Material Science and Technology
Abstract:Laser powder bed fusion(L-PBF) of Sc/Zr-modified Al-based alloys has recently become a promising method for developing a new generation of high-performance Al alloys. To clarify the modification roles of Sc/Zr elements, an Al–4.66Mg–0.48Mn–0.72Sc–0.33Zr(wt.%) alloy was processed using L-PBF. The effect of the local solidification condition of the molten pool on the precipitation behavior of primary Al 3 (Sc,Zr) was analyzed based on time-dependent nucleation theory. It was found that primary Al 3 (Sc,Zr)inevitably precipitated at the fusion boundary, while its precipitation could be effectively suppressed in the inner region of the molten pool. This subsequently induced the formation of a heterogeneousα-Al matrix. After direct aging, the heredity of solidification microstructure introduced heterogeneous secondary Al 3 (Sc,Zr) precipitates within α-Al matrix. Owing to the inverse relationship between grain boundary strengthening and precipitation strengthening, the direct-aged sample with dual heterogeneous structures exhibited reduced mechanical heterogeneity, resulting in lowered hetero-deformation-induced hardening. The low strain-hardening capability in the direct-aged sample promoted necking instability while inducing a large Lüders elongation, which effectively improved the tensile ductility.
What problem does this paper attempt to address?