Abstract:A series of semi-interpenetrating polymer network anion exchange membranes (semi-IPN AEMs), composed of a quaternized poly(styrene) (PS) copolymer and crosslinked poly(2,6-dimethyl-1,4-phenylene oxide) (PPO) networks, have been designed and fabricated. In this system, quaternized PS served as an anion transport moiety, while crosslinked PPO networks formed by azide–alkyne cycloaddition under an organic base were expected to maintain the mechanical properties and dimensional stability of the resulting semi-IPN AEMs. The semi-IPN AEMs showed improved mechanical properties compared to the control sample prepared by physical blending without crosslinking. It was found that the sIPN-62/30 AEM with an IEC of 1.44 meq. g−1 showed the highest hydroxide conductivity of 37.2 mS cm−1 at 20 °C and a relatively low swelling ratio of 12% at 20 °C in water. Further increasing the fraction of the linear conductive component (sIPN-75/20) led to a dramatic increase of water uptake, which diluted the ion concentration in the AEMs, consequently decreasing the hydroxide conductivity of the membrane (28 mS cm−1 at 20 °C). However, a high mechanical strength and low swelling ratio were observed for sIPN-75/20 samples due to the presence of hydrophobic crosslinked PPO networks. The alkaline stability of the semi-IPN AEMs was evaluated in 1 M NaOH at 80 °C. 59.1%, 86.7% and 74.8% retention in hydroxide conductivity, weight and IEC values were recorded for the sIPN-62/30 AEM respectively after 700 h testing. This result indicated that the crosslinked networks in semi-IPN AEMs can effectively protect the cations from being attacked by hydroxide ions. A single H2/O2 alkaline fuel cell of the sIPN-62/30 membrane demonstrated that a maximum power density of 110.6 mW cm−2 was achieved at a current density of 280 mA cm−2 at 60 °C. Although a loss of 78.3% of its initial performance was observed for the sIPN-62/30 membrane after 30 h alkaline fuel cell durability testing at 100 mA cm−2, high retention in IEC values and hydroxide conductivity for the aged sIPN-62/30 membrane shows that the semi-IPN AEMs based on BTMA cations are chemically stable under fuel cell operation conditions.

Nafion-Based Proton-Exchange Membranes Built on Cross-Linked Semi-Interpenetrating Polymer Networks Between Poly(acrylic Acid) and Poly(vinyl Alcohol).

Proton exchange membranes based on semi-interpenetrating polymer networks of Nafion ® and poly(vinylidene fluoride) via radiation crosslinking

Poly(vinyl alcohol)/poly(acrylamide-co-diallyldimethylammonium chloride) (PVA/PAADDA) composite as novel anion-exchange membranes for potential use in fuel cells

Novel Interpenetrating Polymer Network Sulfonated Poly (phthalazinone Ether Sulfone Ketone)/polyacrylic Acid Proton Exchange Membranes for Fuel Cell

Proton Exchange Membranes Based on Semi-Interpenetrating Polymer Networks of Fluorine-Containing Polyimide and Nafion®

Polyamide-coated Nafion Composite Membranes with Reduced Hydrogen Crossover Produced Via Interfacial Polymerization

Semi-interpenetrating Polymer Networks Based-on End-Group Crosslinked Fluorine-Containing Polyimide Via Click Chemistry

Proton conducting membranes based on semi-interpenetrating polymer network of Nafion® and polybenzimidazole

Proton exchange membranes based on semi-interpenetrating polymer networks of polybenzimidazole and perfluorosulfonic acid polymer with hollow silica spheres as micro-reservoir

Composite Polymer Electrolyte Membranes Based on Nafion and Modified PVDF Electrospun Nanofiber Mats

Synthesis and Characterization of Nafion/cross-linked PVP Semi-Interpenetrating Polymer Network Membrane for Direct Methanol Fuel Cell

Novel Composite Proton Exchange Membrane with Connected Long-Range Ionic Nanochannels Constructed Via Exfoliated Nafion-Boron Nitride Nanocomposite.

Incorporating Phosphoric Acid-Functionalized Polydopamine into Nafion Polymer by in Situ Sol-Gel Method for Enhanced Proton Conductivity

Hydrophilic Cross-Linked Aliphatic Hydrocarbon Diblock Copolymer as Proton Exchange Membrane for Fuel Cells

Nafion Composite Membranes Impregnated with Polydopamine and Poly(Sulfonated Dopamine) for High-Performance Proton Exchange Membranes.

Composite membranes of Nafion and poly(styrene sulfonic acid)-grafted poly(vinylidene fluoride) electrospun nanofiber mats for fuel cells

Proton-Conducting Poly-γ-glutamic Acid Nanofiber Embedded Sulfonated Poly(ether Sulfone) for Proton Exchange Membranes.

Enhanced properties of Nafion nanofibrous proton exchange membranes by altering the electrospinning solvents

Semi-interpenetrating polymer networks of poly (vinyl alcohol)-functionalized nanocrystals/sulfonated poly (ether ether ketone) (PVA-FNCs/SPEEK) as fuel cell membrane

Nafion based semi-interpenetrating polymer network membranes from a cross-linkable SPAEK and a fluorinated epoxy resin for DMFCs

Semi-interpenetrating polymer networks by azide–alkyne cycloaddition as novel anion exchange membranes