Abstract:The “HOPE-I” type high-current pulsed electron beam (HCPEB) equipment was used to irradiate the pure aluminum material with Zr coating preset by ball milling to realize the alloying of a Zr–Al coating surface. The microstructure and phase analysis were conducted by XRD, SEM, and TEM. The experimental results show that after Zr alloying on the Al surface by HCPEB, a layer of 15 μm was formed on the surface of the sample, which was mainly composed of Zr and Al–Zr intermetallic compounds. A large number of Al3Zr (Ll2) particles was uniformly distributed in the alloyed layer, and the Al grains were obviously refined. In addition, the surface hardness and corrosion resistance of the samples were improved significantly after HCPEB irradiation.
materials science, multidisciplinary,physics, applied,nanoscience & nanotechnology,chemistry
What problem does this paper attempt to address?
This paper attempts to achieve Zr alloying on the surface of pure aluminum using High Current Pulsed Electron Beam (HCPEB) technology to improve its surface properties, particularly hardness and corrosion resistance. Specifically, the researchers used the "HOPE-I" type high current pulsed electron beam equipment to irradiate pure aluminum materials pretreated by ball milling, studying the microstructure and performance changes of the Zr alloying layer by varying the number of irradiation pulses.
### Main Issues of the Paper:
1. **Improving Surface Properties**: How to form a Zr alloying layer on the surface of pure aluminum through high current pulsed electron beam irradiation technology, thereby significantly improving its surface hardness and corrosion resistance.
2. **Microstructure Analysis**: Studying the microstructure and phase composition of the Zr alloying layer through X-ray diffraction (XRD), scanning electron microscopy (SEM), and transmission electron microscopy (TEM).
3. **Optimizing Irradiation Parameters**: Determining the optimal number of irradiation pulses to achieve the best surface properties and microstructure.
### Research Methods:
1. **Sample Preparation**: Processing pure aluminum materials into square plates of 10 × 10 × 5 mm and pre-depositing a Zr coating on their surface through ball milling.
2. **Irradiation Treatment**: Using the "HOPE-I" type high current pulsed electron beam equipment to irradiate the samples, with the number of irradiation pulses being 10, 20, 30, and 40 times respectively.
3. **Microstructure Characterization**: Analyzing the microstructure and phase composition of the irradiated samples through XRD, SEM, and TEM.
4. **Performance Testing**: Testing the surface hardness and corrosion resistance of the samples through microhardness measurement and electrochemical workstation.
### Main Results:
1. **Microstructure Changes**: With the increase in the number of irradiation pulses, the Zr element gradually dissolves into the aluminum matrix, forming a large amount of Al₃Zr (Ll₂) phase. When the number of irradiation pulses reaches 30 times, the content of the Al₃Zr phase reaches its maximum, and the surface microstructure is uniform.
2. **Surface Performance Improvement**: After 30 irradiations, the surface hardness and corrosion resistance of the samples are significantly improved, and the surface roughness is reduced to the minimum.
3. **Optimal Irradiation Parameters**: 30 irradiations are the optimal irradiation parameters to achieve the best surface properties and microstructure. Exceeding 30 irradiations will lead to surface quality deterioration, with more small pits and Zr-depleted areas appearing.
### Conclusion:
Achieving Zr alloying on the surface of pure aluminum through high current pulsed electron beam irradiation technology can significantly improve its surface properties, especially in terms of hardness and corrosion resistance. The optimal number of irradiation pulses is 30 times, at which the Al₃Zr phase is formed the most, and the surface microstructure is uniform, with the best performance.