Abstract:As a kind of ferroelectric and antiferromagnetic coexistent multi-ferroic material, BiFeO3 (BFO) has a theoretical saturation polarization over 100 μC/cm2, and a Curie temperature of 830 ℃, which may offer a huge electrocaloric effect. However, owing to the evaporation of Bi2O3 in the sintering process at high temperatures and the variation of chemical valence of iron ions, there are lots of point defects and also a large leakage current existing in BFO, making the ferroelectricity of BFO hard to develop and measure. Although the forming of solid solution with BaTiO3 (BTO) or other oxide ferroelectrics may mitigate the leakage current, high loss tangent is still existent. This work tries to address this issue by adding manganese ions into the BFO-BTO solid solution. The 0.7(BFO)-0.3(BTO)+x%MnO2 ceramics are prepared through using the conventional solid-state reaction at high temperature. The microstructure, dielectric characteristic and ferroelectric characteristic are investigated by doping different Mn4+ ions. Results indicate that the crystallographic structure is of rhombohedral and pseudocubic phase coexistence. It is observed that a certain content of Mn4+ ions may lead both the loss tangent and the leakage current for BFO-BTO ceramic to decrease, which is due to the compensation of dopant Mn4+ ions for the oxygen vacancies. In addition, the 0.7BFO-0.3BTO+0.5%MnO2 ceramic arrives at a maximum polarization of 50.53 μC/cm2 at 100 kV/cm. Finally, a direct approach is used to measure the electrocaloric effect. It is found that using the polarization flip method, the ECE temperature change is observed to increase almost 8 times when the electric field changes from 0 to –30 kV/m with respect to that when the electric field decreases from 30 kV/cm to 0. This verifies that the Lu et al’s method is also applicable to polycrystalline first-order phase transition ferroelectrics.

Giant Electrocaloric Effect in BiFeO3 and La Codoped PbZr0.7Ti0.3O3 Epitaxial Thin Films in a Broad Temperature Range

Giant negative electrocaloric effect in antiferroelectric PbZrO3 thin films in an ultra-low temperature range

Negative/Positive Electrocaloric Effect in Single-Layer Pb(ZrₓTi1–x )O₃ Thin Films for Solid-State Cooling Device

Giant Electrocaloric Effect in Ferroelectric Ultrathin Films at Room Temperature Mediated by Flexoelectric Effect and Work Function

Large Room Temperature Electrocaloric Effect in PbZrO3/ Ca3Mn2O7 Heterostructure

Thermal Strain Induced Large Electrocaloric Effect of Relaxor Thin Film on LaNiO3/Pt Composite Electrode with the Coexistence of Nanoscale Antiferroelectric and Ferroelectric Phases in a Broad Temperature Range

Large room temperature electrocaloric effect in PbZrO3/Ca3Mn2O7 heterostructure

Giant Electrocaloric Effect in BaZr 0 . 2 Ti 0 . 8 O 3 Thick Film

Giant electrocaloric effect in PZT bilayer thin films by utilizing the electric field engineering

Large Electrocaloric Effect in (bi0.5na0.5)0.94ba0.06tio3 Lead-Free Ferroelectric Ceramics by La2O3 Addition

Giant Electrocaloric Effect Enhancement Due to the Polarization Flip and Influence of Mn4+ Doping on the Dielectric, Ferroelectric Properties in 0.7Bifeo3-0.3Batio3 Ceramics

Large Electrocaloric Effect in (Bi0.5na0.5)tio3-Based Relaxor Ferroelectrics

Electric Field Induced Phase Transitions And Electrocaloric Effect Of La3+ Doped Pb(Zr,Sn,Ti)O-3 Ceramics

Adjustable Giant Negative Electrocaloric Effect in Pb1+xZrO3 Thin Films

Large Electrocaloric Effect in Ba(Ti1−xSnx)O3 Ceramics over a Broad Temperature Region

Giant negative electrocaloric effect in antiferroelectric La-modified PbZrO3 thin films within wide temperature range

Giant Electrocaloric Response over A Broad Temperature Range in Modified BaTiO3 Ceramics

Manipulation of Curie temperature and ferroelectric polarization for large electrocaloric strength in BaTiO<sub>3</sub>-based ceramics

Giant Electrocaloric Effect In Lead-Free Thin Film Of Strontium Bismuth Tantalite

Synergy of Ferroelectric-Relaxor Transition and Multiphase Coexistence Induced High Electrocaloric Effect with Wide Temperature Span in Pb0.7Ba0.3ZrO3-based System

Giant Electrocaloric Effect in Compositionally Graded PZT Multilayer Thin Films