Abstract:N-doped Ce0.2Zr0.8O2 catalysts for NO oxidation were successfully fabricated via NH3 treatment at high temperature, and the N doping amount could be controlled via adjusting the conditions of various NH3 concentrations and treatment times. The optimal 10N700-5 catalyst revealed the sensational oxidation efficiency at low temperature, which surpassed 50% at 180 °C and reached up to 82.82% at 270 °C. The excellent activity was ascribed to the numerous generations of O2– and the accompanied vast formation of Cr6+, caused by N doping. N atoms were doped in Ce0.2Zr0.8O2 in the structure of Ce–O–N–O–Zr via the O–N–O bond between N and O. The analysis of affecting factors elucidated that cation ratios played a more significant role than the Brunauer–Emmett–Teller surface area, and Cr6+ ratios acted mostly. Additionally, the conceivable promotion mechanism by N doping for NO oxidation was examined via in situ DRIFTS. This work propelled denitration with the selective catalytic oxidation technique for industrial application and lent a novel perspective for the design of catalysts with satisfied oxidation efficiency at low temperature.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acs.energyfuels.0c03645?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acs.energyfuels.0c03645</a>.Procedures of characterizations and catalytic oxidation of NO test, durability test over the 10N700-5 sample, and XRD and XPS over the fresh and used 10N700-5 sample (<a class="ext-link" href="/doi/suppl/10.1021/acs.energyfuels.0c03645/suppl_file/ef0c03645_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.

Improved Pd/CeO2 Catalysts for Low-Temperature NO Reduction: Activation of CeO2 Lattice Oxygen by Fe Doping.

Improved Pd/CeO 2 Catalysts for Low-Temperature NO Reduction: Activation of CeO 2 Lattice Oxygen by Fe Doping

Engineering bifunctional Pd/CeNbTiOx catalyst for the simultaneous removal of NO and CO under oxygen-rich conditions at low temperature

CeO2 doping boosted low-temperature NH3-SCR activity of FeTiOx catalyst: A microstructure analysis and reaction mechanistic study

Synergistic Effects of Ternary PdO-CeO2-OMS-2 Catalyst Afford High Catalytic Performance and Stability in the Reduction of NO with CO

An Excellent Support of Pd–Fe–Ox Catalyst for Low Temperature CO Oxidation: CeO2 with Rich (200) Facets

Fe decorated CeO2 microsphere catalyst with surface oxygen defect for NO reduction by CO

Doped-Nd Enhanced the Performance of FeCoMnCe Catalyst on the NOx Selective Catalytic Reduction

Revealing the Excellent Low-Temperature Activity of the Fe 1- x Ce x O δ -S Catalyst for NH 3 -SCR: Improvement of the Lattice Oxygen Mobility

Promotional Effect of Ce on Iron-Based Catalysts for Selective Catalytic Reduction of NO with NH3

Constructing Efficient CuO -Ceo2 Catalyst for NO Reduction by CO: New Insights into the Structure–activity Relationship

Preparation and Investigation of Iron–Cerium Oxide Compounds for NOx Reduction

Doping Pd2+ into NinCeOx Nanofibers Promotes Low-Temperature CO2 Methanation

Increasing Cerium Dispersion Favours Lattice Oxygen Activity of Cobalt Oxides for CO Catalytic Combustion

Influence of Oxygen Vacancy-Induced Coordination Change on Pd/CeO2 for NO Reduction

Fabrication of Controllable N-Doped Ce 0.2 Zr 0.8 O 2 via O–N–O Bond with Robust NO Oxidation and Durability at Low Temperature

Activity Test and Mechanism Study of 3DOM Ce 0.8 M 0.1 Zr 0.1 O 2 (M=Cr, Sn, Fe, Co, Ni, Mn, Cu) Catalyst in the Selective Catalytic Reduction of NO by CO**

Influence of Oxygen Vacancy-Induced Coordination Change on Pd/CeO2 for NO Reduction.

Nickel foam supported CuCe mixed metal oxide as monolith catalyst for NO removal

Revealing the Excellent Low-Temperature Activity of the Fe1–xCexOδ-S Catalyst for NH3-SCR: Improvement of the Lattice Oxygen Mobility

Insight into the mechanisms of activity promotion and SO2 resistance over Fe-doped Ce-W oxide catalyst for NO reduction