Understanding and Preventing Lubrication Failure at the Carbon Atomic Steps
Wenmeng Yan,Fakhrul H. Bhuiyan,Chuan Tang,Liang Wei,Yilong Jiang,Seokhoon Jang,Yangqin Liu,Jiang Wu,Wen Wang,Yang Wang,Ashlie Martini,Linmao Qian,Seong H. Kim,Lei Chen
DOI: https://doi.org/10.1002/smll.202301515
IF: 13.3
2023-05-12
Small
Abstract:At the graphene step edge, the armchair (AC) structure gives only a minor topographic effect on friction, while the zigzag (ZZ) structure induces friction two orders of magnitude larger than the basal friction. The high‐friction ZZ edge becomes superlubricious through reconstructing to the (5,7) azulene‐like structure upon thermal annealing in an inert gas environment. Two‐dimensional (2D) lamellar materials are normally capable of rendering super‐low friction, wear protection, and adhesion reduction in nanoscale due to their ultralow shear strength between two basal plane surfaces. However, high friction at step edges prevents the 2D materials from achieving super‐low friction in macroscale applications and eventually leads to failure of lubrication performance. Here, taking graphene as an example, the authors report that not all step edges are detrimental. The armchair (AC) step edges are found to have only a minor topographic effect on friction, while the zigzag (ZZ) edges cause friction two orders of magnitude larger than the basal plane. The AC step edge is less reactive and thus more durable. However, the ZZ structure prevails when step edges are produced mechanically, for example, through mechanical exfoliation or grinding of graphite. The authors found a way to make the high‐friction ZZ edge superlubricious by reconstructing the (6,6) hexagon structure to the (5,7) azulene‐like structure through thermal annealing in an inert gas environment. This will facilitate the realization of graphene‐based superlubricity over a wide range of industrial applications in which avoiding the involvement of step edges is difficult.
materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,nanoscience & nanotechnology