Ammonia Nitrogen Removal from Coking Wastewater and High Quality Gypsum Recovery by Struvite Recycling by Using Calcium Hydroxide As Decomposer

Haiming Huang,Bing Li,Jiankun Dai,Wenjun Wang,Minge Zhang,Yangzhu Ou

DOI: https://doi.org/10.1016/j.jenvman.2021.112712

IF: 8.7

2021-01-01

Journal of Environmental Management

Abstract:This study deals with the highly significant and cost-effective pretreatment of the high concentration of the Total Ammonia Nitrogen (TAN) in coking wastewater to improve the biodegradability. Struvite crystallization is a promising process for TAN removal, but the high operating cost hinders its application. To solve this problem, a novel struvite recycling process was proposed for pre-treating TAN present in the coking wastewater, within which struvite was decomposed in the solid-liquid system using Ca(OH)(2) as the decomposer. The results indicates that 91% of ammonium in struvite could be stripped out from the decomposition solution, with Ca(OH)(2):NH4+ in the molar ratio of 2:1, temperature at 35 degrees C and a gas to liquid volume ratio of 3500. The resulting solution, post the escape of the ammonia, was dissolved by sulfuric acid. Approximately 100% of the phosphate and magnesium were observed to be released from the insoluble phosphate compounds, resulting in the formation of high-purity gypsum. A TAN removal efficiency of 89% could be achieved by reusing the supernatant after the dissolution of the decomposition product, at pH 9.5 and the Mg:TAN:PO4-P molar ratio of 1.2:1:1. The pilot-scale test demonstrated that approximately 86% TAN was removed from the coking wastewater and the purity of recovered could reach over 99%. Further economic analysis proves that the operation cost of the proposed process is 0.55$ per m(3) of coking wastewater, showing a 73% cost reduction when compared to struvite crystallization without recycling.