Abstract:In the classical planar heterojunction perovskite solar cells (PSCs), the electron conducting TiO2 layer shows lower conductivity than the hole transporting materials such as spiro-OMeTAD, which becomes one of the key problems in improving the power conversion efficiency (PCE) of PSCs. In this study, the surface of compact TiO2 layer is modified by a thin self-assembled dodecanedioic acid (DDDA) molecular layer. The TiO2 substrates are immersed into the DDDA solution for 0.5, 2.5, 4.5, 22 h, respectively. It is found that the PCE of PSCs is improved when using the DDDA modified TiO2, showing optimized PCE of 15.35% +/- 0.75% under AM 1.5G illumination at 100 mW.cm(-2) after 4.5 h modification. The short current density (J(SC)) of the best device is improved from 20.34 mA.cm(-2) to 23.28 mA.cm(-2), with the PCE increasing from 14.17% to 15.92%. And it is found that the hysteresis of the PSC is also reduced remarkably with hysteresis index decreasing from 0.4288 to 0.2430. In the meantime, the device with DDDA modification shows a significant improvement in light stability, keeping 71% of its initial PCE value after 720 min exposure under AM 1.5G illumination at 100 mW.cm(-2) without encapsulation. As a contrast, the device without DDDA modification keeps 59% of its initial PCE value under the same condition. To reveal the mechanism, we investigate the surface energy level change using ultraviolet photoemission spectroscopy. It is found that after DDDA modification, the valence-band maximum energy (E-VBM) of TiO2 decreases from -25 eV to -32 eV, and the conduction-band minimum energy (E-CBM) of TiO2 from -05 eV to -12 eV. The shifting of energy level optimizes the energy level alignment at the interface between the TiO2 and perovskite. It promotes the transport of electrons from perovskite layer to compact TiO2 layer and obstructs the transport of holes from perovskite layer to compact TiO2 layer more effectively. In addition, the decrease of E-CBM implies the increase of conductivity of TiO2. We further design a series of electrical experiments, and confirm that the modification improves the conductivity of TiO2 obviously with both contact resistance and thin-film resistance decreasing. In summary, our results indicate the enormous potential of the compact TiO2 layer with a thin self-assembled DDDA molecular layer modification to construct efficient and stable planar heterojunction PSCs for practical applications.

Surface Modification of TiO2 for Perovskite Solar Cells

TiO2 modification with multi-acid treatment for efficient interfacial perovskite-TiO2 electron transport

Charge transfer enhancement of TiO2/perovskite interface in perovskite solar cells

Modification of SnO2 electron transport Layer: Brilliant strategies to make perovskite solar cells stronger

Recent Advances in Metal Oxide Electron Transport Layers for Enhancing the Performance of Perovskite Solar Cells

Low‐Temperature in Situ Amino Functionalization of TiO2 Nanoparticles Sharpens Electron Management Achieving over 21% Efficient Planar Perovskite Solar Cells

Improvement of current characteristic of perovskite solar cells using dodecanedioic acid modified TiO2 electron transporting layer

Interfacial Crosslinking for Efficient and Stable Planar TiO2 Perovskite Solar Cells

In Situ Surface Fluorination of TiO 2 Nanocrystals Reinforces Interface Binding of Perovskite Layer for Highly Efficient Solar Cells with Dramatically Enhanced Ultraviolet‐Light Stability

Bifunctional Interface Engineering by Oxidating Layered TiSe 2 for High-Performance CsPbBr 3 Solar Cells

Energy Level Modulation of TiO2 Using Amino Trimethylene Phosphonic Acid for Efficient Perovskite Solar Cells with Average VOC of 1.19 V

Room-temperature processed TiO2 to construct composite electron transport layers for efficient planar perovskite solar cells

Enhancing Perovskite Solar Cell Performance Through Surface Engineering of Metal Oxide Electron-Transporting Layer

Dual Interfacial Modification Engineering with 2D MXene Quantum Dots and Copper Sulphide Nanocrystals Enabled High‐Performance Perovskite Solar Cells

Interface engineering at electron transport/perovskite layers using wetting mesoporous titanium dioxide to fabricate efficient and stable perovskite solar cells

Interface Modification Using Li-Doped Hollow Titania Nanospheres for High-Performance Planar Perovskite Solar Cells

TiO2/SnO2 Bilayer Electron Transport Layer for High Efficiency Perovskite Solar Cells

Interface Engineering of TiO2/perovskite Interface Via Fullerene Derivatives for High Performance Planar Perovskite Solar Cells

Improving the Electron Transport Performance of TiO2 Film by Regulating TiCl4 Post‐Treatment for High‐Efficiency Carbon‐Based Perovskite Solar Cells

Effect of oxidized CdO quantum dots doped TiO2 electron transport layer on performance of mesoporous perovskite solar cells

Colloidal TiO2-Modified Mesoporous Electron Transport Layer in Perovskite Solar Cells