Mechanically Robust Microporous Anion Exchange Membranes with Efficient Anion Conduction for Fuel Cells

Tong Huang,Junfeng Zhang,Yabiao Pei,Xin Liu,Jiandang Xue,Haifei Jiang,Xiaoyu Qiu,Yan Yin,Hong Wu,Zhongyi Jiang,Michael D. Guiver
DOI: https://doi.org/10.1016/j.cej.2021.129311
IF: 15.1
2021-01-01
Chemical Engineering Journal
Abstract:Polymers of intrinsic microporosity (PIMs) present an attractive opportunity for developing new types of anion exchange membranes (AEMs) for fuel cell featuring charged subnanometer-sized micropores. But challenges exist to make mechanically robust PIM AEMs due to their high chain rigidity. Imparting more flexibility improves mechanical properties but sacrifices microporosity. Here, a mechanically robust and highly anion conductive PIM AEM (QPIM-1) fabricated by facile animation and quaternization of PIM-1 membrane is reported, and its structure-property relationships are investigated, especially focusing on the microporous structure. High molecular weight alleviates brittleness, as QPIM-1 AEM shows comparable mechanical properties to conventional AEMs, quaternized poly(2,6-dimethyl-1,4-phenylene oxide) (QPPO), at a membrane thickness down to -35 mu m and a high ion exchange capacity (IEC) up to -2.1 mmol g-1. The micropores situated among the rigid and contorted polymer chains evolve into water/ion conduction channels when the membrane is hydrated. This results in improved morphology over dense polymeric AEMs by less hindered ion pathways. QPIM-1 AEMs exhibit superior ion conduction efficiency, which is 2.6-5.3 times that of dense QPPO AEM at similar ion exchange capacities (IECs). A high hydroxide ion conductivity of 57 mS cm-1 at 20 ?C is obtained, which is among the highest reported anion conductive PIM-based AEMs. Even though the AEMs are microporous, only slight H2 permeation is observed when hydrated and at high open circuit voltage (OCV) of a single fuel cell.
What problem does this paper attempt to address?