Low Cycle Fatigue Behavior of GH3536 Alloy Formed Via Laser Additive Manufacturing
Xiao Lairong,Tan Wei,Liu Liming,Tu Xiaoxuan,Peng Zhenwu,Wang Huan,Zhao Xiaojun
DOI: https://doi.org/10.3788/cjl202148.2202009
2021-01-01
Chinese Journal of Lasers
Abstract:Objective In recent years, additive manufacturing of GH3536 alloy has made it an appealing nickel-base superalloy for aircraft engine applications. At the moment, much attention is being paid to the as-deposited alloy, with particular emphasis on the forming process, microstructure, and tensile properties. However, there are only a few reports on low cycle fatigue properties in the open literature. The anisotropic fatigue properties of as-deposited alloys have been demonstrated. Furthermore, the as-deposited alloy's flaws will considerably reduce its fatigue lifetime. Fortunately, hot isostatic pressing (HIP) and solution treatment ( ST) are viable methods for improving the alloy's fatigue properties. The goal of this study is to evaluate the low cycle fatigue properties of GH3536 alloy treated with HIP and ST at room temperature and 800 t , as well as to identify the deformation and fracture mechanisms. In addition, a plastic strain energy model for predicting fatigue lifetime is developed. Methods GH3536 alloy was prepared using Farsoon FS 271m selective laser melting equipment with argon gas protection. The HIP was performed in QIH-62 equipment for 3 h at 1175 t under a pressure of 160 MPa in a vacuum environment, after which the alloy was furnace-cooled to room temperature. ST was performed in SX-12-16 equipment at 1175 t in a vacuum environment for 2 h, followed by argon cooling. Low cycle fatigue specimens were processed according to GB/T 15248-2008 and tested on MTS 810 fatigue testing machine at room temperature and 800 t under strain control. The loading waveform was a triangular wave; the total strain amplitude was 0.25%-1.2%; the strain rate was 0. 01 s(-1), and the strain ratio was - 1. The TESCAN MIRA3 scanning electron microscopy was used to examine the fracture morphology of the fatigue specimens, and the Tecnai G2 20 transmission electron microscope was used to examine the microstructure after the fatigue test. Results and Discussions Temperature and strain amplitude appear to have an impact on fatigue life and cyclic deformation behavior. The fatigue life of the alloy at room temperature is greater than that at 800 degrees C. At room temperature, the alloy exhibits cyclic hardening before cyclic softening. However, at 800 degrees C, the specimens with 0.25% and 0.4% strain amplitudes show cyclic hardening at first, cyclic stabilization subsequently, and then cyclic softening until the final rupture. After cyclic hardening, the specimens with 0.8 Yo and 1.2 Yo strain amplitudes only show softening (Fig. 3) . The Basquin-Coffin-Manson model accurately describes the relationship between total strain amplitude, elastic strain amplitude, plastic strain amplitude, and fatigue cycles. The transition fatigue life at room temperature and 800 degrees C calculated using the Basquin-Coffin-Manson model is 12399 and 1152 cycles, respectively (Fig. 6) . At room temperature, the fracture morphology exhibits a single fatigue source that originates from the resident slip band near the surface of the specimen (Fig. 7) . Whereas, at 800 degrees C, multicrack sources usually derived from defects near the surface can be observed ( Fig. 8) . The increase in dislocation density at room temperature makes dislocation slip more difficult and increases the alloy's cyclic hardening degree ( Fig. 9 ) . As a result of dynamic recovery, the density of dislocations at 800 degrees C is lower than that at room temperature. High temperature and dislocations promote the heterogeneous nucleation of precipitates. Therefore, the interaction between precipitates and dislocations results in cyclic hardening of the alloy (Fig. 10) . The plastic strain energy model is used to predict the life of the alloy. The intrinsic fatigue toughness ( W-0) and fatigue transition exponent (beta) are 222.24 MJ/m(3) and 2.320 at room temperature and 673.15 MJ/m(3) and 1.225 at 800 degrees C, respectively. The predicted lifetime is within 1.5 times of the dispersion band (Fig. 11). Conclusions The fatigue lifetime of GH3536 alloy treated with HIP and ST decreases as temperature or strain amplitude increases. At room temperature, the alloy undergoes cyclic hardening before cyclic softening at various strain amplitudes, and its fatigue crack source is a single one. The increase of the dislocation density is an important factor of cyclic hardening. However, at 800 degrees C , the alloy initially exhibites cyclic hardening, then cyclic stabilization, and finally cyclic softening to failure at low strain amplitude. Meanwhile, at high strain amplitudes, the alloy exhibits cyclic softening after cyclic hardening. Furthermore, on the fracture surface of the fatigue alloy tested at 800 degrees C, a number of crack sources are observed. The alloy hardens due to the pinning effect of the precipitated phases. The alloy's fatigue lifetime and strain amplitude satisfy the Basquin-Coffin-Manson equation, and the transition fatigue lifetime at room temperature and 800 degrees C is 12399 and 1152 cycles, respectively. The plastic strain energy model accurately predicts fatigue life, and the predicted results are within 1.5 times of the dispersion band.