Tunable magnetic and microwave absorption properties of barium ferrite particles by site-selective Co 2+ -Zr 4+ Co-doping
Xinyang Wang,Bo Wang,Shicheng Wei,Yujiang Wang,Yi Liang,Linwei Li
DOI: https://doi.org/10.1016/j.jallcom.2023.170777
IF: 6.2
2023-06-06
Journal of Alloys and Compounds
Abstract:Co 2+ -Zr 4+ ion-doped barium ferrite (BaFe 12–2x (CoZr) x O 19 , x = 0.3, 0.4, 0.5) particles were prepared by a citrate sol-gel method. It is found that a single M-type barium ferrite phase exists in particles fabricated with a relatively high ion doping amount, which indicates Co 2+ ions can balance the system valence and aid the entry of high-valent Zr 4+ ions. With the increase in doping amount, the lattice constant and the particle size gradually increase. Moreover, the content of Fe 2+ is at a lower level, and the oxygen vacancy concentration first increases and then plateaus. According to the results of first-principles calculation and Mössbauer spectral analysis, doping ions tend to replace Fe 3+ at 4 f 2 , 4 f 1 , and 2b sites, continuously decreasing the coercivity and saturation magnetization. Multi-doping effectively introduces dual magnetic resonances and multiple polarization, and reduces the natural resonance frequency. In addition, it improves the impedance matching performance and the electromagnetic attenuation capabilities, leading to an excellent absorption performance in the Ku-band. The co-doped barium ferrites produce obvious interference cancellation at a specific thickness, further improving the absorption ability. The BaFe 11 Co 0.5 Zr 0.5 O 19 can achieve the maximum microwave absorption bandwidth of 6.08 GHz, covering the entire Ku-band. When the matching thickness is 2.05 mm, it also exhibits the minimum reflection loss of − 48.16 dB at 11.94 GHz. The above results suggest that this co-doped barium ferrite possesses great potential in microwave absorption applications.
materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering